材料说明：主要特点：
•韧性高，即使在较低的温度下
•高尺寸精度和稳定性
•油漆性能良好
•流动性好
等级特征：
•阻燃
•注塑
上海松翰塑化科技有限公司，供应产品，品质一流,物美价廉。tpu、tpv、pa、pc、pc/abs、lcp、种类齐全。欢迎广大客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
Physical PropertiesMetricEnglishCommentsDensity 1.18 g/cc0.0426 lb/in³ISO 1183-1Moisture Absorption at Equilibrium 0.20 %0.20 %ISO 62, 50% RHWater Absorption at Saturation 0.50 %0.50 %ISO 62Viscosity 155000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C155000 cP
@Shear Rate 1000 1/s,
Temperature 500 °Fmelt viscosity; b.o. ISO 11443-ALinear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
@Thickness 3.00 mm0.0050 - 0.0070 in/in
@Thickness 0.118 in150x105x3mm; b.o. ISO 2577Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
@Thickness 3.00 mm0.0050 - 0.0070 in/in
@Thickness 0.118 in150x105x3mm; b.o. ISO 2577 Mechanical PropertiesMetricEnglishCommentsTensile Strength at Break 45.0 MPa6530 psi50 mm/min; ISO 527-1,-2Tensile Strength, Yield 60.0 MPa8700 psi50 mm/min; ISO 527-1,-2Elongation at Break >= 40 %>= 40 %50 mm/min; b.o. ISO 527-1,-2Elongation at Yield 3.5 %3.5 %50 mm/min; ISO 527-1,-2Tensile Modulus 2.60 GPa377 ksi1 mm/min; ISO 527-1,-2Izod Impact, Notched (ISO) 10.0 kJ/m²
@Temperature -30.0 °C4.76 ft-lb/in²
@Temperature -22.0 °FISO 180-A 20.0 kJ/m²
@Temperature 23.0 °C9.52 ft-lb/in²
@Temperature 73.4 °FISO 180-AIzod Impact, Unnotched (ISO) NB
@Temperature 23.0 °CNB
@Temperature 73.4 °FISO 180-U Thermal PropertiesMetricEnglishCommentsCTE, linear, Parallel to Flow 76.0 µm/m-°C
@Temperature 23.0 - 55.0 °C42.2 µin/in-°F
@Temperature 73.4 - 131 °FISO 11359-1,-2CTE, linear, Transverse to Flow 80.0 µm/m-°C
@Temperature 23.0 - 55.0 °C44.4 µin/in-°F
@Temperature 73.4 - 131 °FISO 11359-1,-2Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C203 °FISO 75-1,-2Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C185 °FISO 75-1,-2Vicat Softening Point 100 °C
@Load 5.10 kg212 °F
@Load 11.2 lb50°C/h; ISO 306 102 °C
@Load 5.10 kg216 °F
@Load 11.2 lb120°C/h; ISO 306Flammability, UL94 V-1
@Thickness 1.50 mmV-1
@Thickness 0.0591 in V-0
@Thickness 3.00 mmV-0
@Thickness 0.118 in Processing PropertiesMetricEnglishCommentsMelt Temperature 240 °C464 °FInjection molding; ISO 294Mold Temperature 80.0 °C176 °FInjection molding; ISO 294Injection Velocity 240 mm/sec9.45 in/secISO 294
@Shear Rate 1000 1/s,
Temperature 260 °C155000 cP
@Shear Rate 1000 1/s,
Temperature 500 °Fmelt viscosity; b.o. ISO 11443-ALinear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
@Thickness 3.00 mm0.0050 - 0.0070 in/in
@Thickness 0.118 in150x105x3mm; b.o. ISO 2577Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
@Thickness 3.00 mm0.0050 - 0.0070 in/in
@Thickness 0.118 in150x105x3mm; b.o. ISO 2577 Mechanical PropertiesMetricEnglishCommentsTensile Strength at Break 45.0 MPa6530 psi50 mm/min; ISO 527-1,-2Tensile Strength, Yield 60.0 MPa8700 psi50 mm/min; ISO 527-1,-2Elongation at Break >= 40 %>= 40 %50 mm/min; b.o. ISO 527-1,-2Elongation at Yield 3.5 %3.5 %50 mm/min; ISO 527-1,-2Tensile Modulus 2.60 GPa377 ksi1 mm/min; ISO 527-1,-2Izod Impact, Notched (ISO) 10.0 kJ/m²
@Temperature -30.0 °C4.76 ft-lb/in²
@Temperature -22.0 °FISO 180-A 20.0 kJ/m²
@Temperature 23.0 °C9.52 ft-lb/in²
@Temperature 73.4 °FISO 180-AIzod Impact, Unnotched (ISO) NB
@Temperature 23.0 °CNB
@Temperature 73.4 °FISO 180-U Thermal PropertiesMetricEnglishCommentsCTE, linear, Parallel to Flow 76.0 µm/m-°C
@Temperature 23.0 - 55.0 °C42.2 µin/in-°F
@Temperature 73.4 - 131 °FISO 11359-1,-2CTE, linear, Transverse to Flow 80.0 µm/m-°C
@Temperature 23.0 - 55.0 °C44.4 µin/in-°F
@Temperature 73.4 - 131 °FISO 11359-1,-2Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C203 °FISO 75-1,-2Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C185 °FISO 75-1,-2Vicat Softening Point 100 °C
@Load 5.10 kg212 °F
@Load 11.2 lb50°C/h; ISO 306 102 °C
@Load 5.10 kg216 °F
@Load 11.2 lb120°C/h; ISO 306Flammability, UL94 V-1
@Thickness 1.50 mmV-1
@Thickness 0.0591 in V-0
@Thickness 3.00 mmV-0
@Thickness 0.118 in Processing PropertiesMetricEnglishCommentsMelt Temperature 240 °C464 °FInjection molding; ISO 294Mold Temperature 80.0 °C176 °FInjection molding; ISO 294Injection Velocity 240 mm/sec9.45 in/secISO 294