类别：热塑性聚合物；聚合物；ABS；聚碳酸酯/ ABS合金，无筋；聚碳酸酯（PC）
材料说明：主要特点：
•韧性高，即使在较低的温度下
•高尺寸精度和稳定性
•油漆性能良好
•流动性好
等级特征：
•注塑
•易流动
上海松翰塑化科技有限公司，供应产品，品质一流,物美价廉。tpu、tpv、pa、pc、pc/abs、lcp、种类齐全。欢迎广大客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183-1 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | ISO 62, 50% RH |
| Water Absorption at Saturation | 0.70 % | 0.70 % | ISO 62 |
| Viscosity | 210000 cP @Shear Rate 1000 1/s, Temperature 260 °C |
210000 cP @Shear Rate 1000 1/s, Temperature 500 °F |
melt viscosity; b.o. ISO 11443-A |
| Linear Mold Shrinkage, Flow | 0.0055 - 0.0075 cm/cm @Thickness 3.00 mm |
0.0055 - 0.0075 in/in @Thickness 0.118 in |
150x105x3mm; b.o. ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0055 - 0.0075 cm/cm @Thickness 3.00 mm |
0.0055 - 0.0075 in/in @Thickness 0.118 in |
150x105x3mm; b.o. ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 53.0 MPa | 7690 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; b.o. ISO 527-1,-2 |
| Elongation at Yield | 4.9 % | 4.9 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527-1,-2 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
ISO 180-A |
| 48.0 kJ/m² @Temperature 23.0 °C |
22.8 ft-lb/in² @Temperature 73.4 °F |
ISO 180-A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180-U |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 100 Hz |
2.9 @Frequency 100 Hz |
IEC 60250 |
| 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm @Thickness 1.00 mm |
889 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 |
| 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 250 V | 250 V | Solution A; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 109 °C | 228 °F | ISO 75-1,-2 |
| Vicat Softening Point | 129 °C @Load 5.10 kg |
264 °F @Load 11.2 lb |
50°C/h; ISO 306 |
| 131 °C @Load 5.10 kg |
268 °F @Load 11.2 lb |
120°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 0.850 mm |
HB @Thickness 0.0335 in |
|
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 °C | 500 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Injection Velocity | 240 mm/sec | 9.45 in/sec | ISO 294 |