类别：热塑性聚合物；聚合物；ABS；聚碳酸酯/ ABS合金，无筋；聚碳酸酯（PC）
材料说明：主要特点：
•韧性高，即使在较低的温度下
•高尺寸精度和稳定性
•油漆性能良好
•流动性好
等级特征：
•注塑
金属化•最佳表面质量
上海松翰塑化科技有限公司，供应产品，品质一流,物美价廉。tpu、tpv、pa、pc、pc/abs、lcp、种类齐全。欢迎广大客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
Physical PropertiesMetricEnglishCommentsDensity 1.14 g/cc0.0412 lb/in³ISO 1183-1Moisture Absorption at Equilibrium 0.20 %0.20 %ISO 62, 50% RHWater Absorption at Saturation 0.70 %0.70 %ISO 62Viscosity 190000 cP@Shear Rate 1000 1/s,
Temperature 260 °C190000 cP
@Shear Rate 1000 1/s,
Temperature 500 °Fmelt viscosity; b.o. ISO 11443-ALinear Mold Shrinkage, Flow 0.0055 - 0.0075 cm/cm
@Thickness 3.00 mm0.0055 - 0.0075 in/in
@Thickness 0.118 in150x105x3mm; b.o. ISO 2577Linear Mold Shrinkage, Transverse 0.0055 - 0.0075 cm/cm
@Thickness 3.00 mm0.0055 - 0.0075 in/in
@Thickness 0.118 in150x105x3mm; b.o. ISO 2577 Mechanical PropertiesMetricEnglishCommentsTensile Strength at Break 50.0 MPa7250 psi50 mm/min; ISO 527-1,-2Tensile Strength, Yield 62.0 MPa8990 psi50 mm/min; ISO 527-1,-2Elongation at Break >= 50 %>= 50 %50 mm/min; b.o. ISO 527-1,-2Elongation at Yield 4.7 %4.7 %50 mm/min; ISO 527-1,-2Tensile Modulus 2.50 GPa363 ksi1 mm/min; ISO 527-1,-2Izod Impact, Notched (ISO) 14.0 kJ/m²
@Temperature -30.0 °C6.66 ft-lb/in²
@Temperature -22.0 °FISO 180-A 42.0 kJ/m²
@Temperature 23.0 °C20.0 ft-lb/in²
@Temperature 73.4 °FISO 180-AIzod Impact, Unnotched (ISO) NB
@Temperature 23.0 °CNB
@Temperature 73.4 °FISO 180-U Electrical PropertiesMetricEnglishCommentsVolume Resistivity 1.00e+16 ohm-cm1.00e+16 ohm-cmIEC 60093Surface Resistance 1.00e+17 ohm1.00e+17 ohmIEC 60093Dielectric Strength 45.0 kV/mm
@Thickness 1.00 mm1140 kV/in
@Thickness 0.0394 inIEC 60243-1Comparative Tracking Index 175 V175 VSolution A; IEC 60112 Thermal PropertiesMetricEnglishCommentsCTE, linear, Parallel to Flow 72.0 µm/m-°C
@Temperature 23.0 - 55.0 °C40.0 µin/in-°F
@Temperature 73.4 - 131 °FISO 11359-1,-2CTE, linear, Transverse to Flow 72.0 µm/m-°C
@Temperature 23.0 - 55.0 °C40.0 µin/in-°F
@Temperature 73.4 - 131 °FISO 11359-1,-2Deflection Temperature at 0.46 MPa (66 psi) 127 °C261 °FISO 75-1,-2Deflection Temperature at 1.8 MPa (264 psi) 108 °C226 °FISO 75-1,-2Vicat Softening Point 128 °C
@Load 5.10 kg262 °F
@Load 11.2 lb50°C/h; ISO 306 130 °C
@Load 5.10 kg266 °F
@Load 11.2 lb120°C/h; ISO 306Flammability, UL94 HB
@Thickness 0.850 mmHB
@Thickness 0.0335 in Processing PropertiesMetricEnglishCommentsMelt Temperature 260 °C500 °FInjection molding; ISO 294Mold Temperature 80.0 °C176 °FInjection molding; ISO 294Injection Velocity 240 mm/sec9.45 in/secISO 294