Tristar® PC-10FR-(VIK) 16 MFI_产品资讯

生产厂家：Information provided by Polymer Technology and Services, LLC (PTS).

生产型号：Tristar® PC-10FR-(VIK) 16 MFI

Physical Properties	Metric	English	Comments
Density	1.23 g/cc	0.0444 lb/in³	ASTM D792
Water Absorption	0.18 %	0.18 %	24 Hrs; ASTM D570
Melt Flow	16 g/10 min @Load 1.20 kg, Temperature 300 °C	16 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM 1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	120	120	ASTM D785
Tensile Strength, Yield	55.2 MPa @Thickness 3.17 mm	8000 psi @Thickness 0.125 in	ASTM D638
Elongation at Break	75 % @Thickness 3.17 mm	75 % @Thickness 0.125 in	ASTM D638
Flexural Yield Strength	86.2 MPa @Thickness 3.17 mm	12500 psi @Thickness 0.125 in	ASTM D790
Flexural Modulus	2.07 GPa @Thickness 3.17 mm	300 ksi @Thickness 0.125 in	ASTM D790
Izod Impact, Notched	6.41 J/cm @Thickness 3.17 mm	12.0 ft-lb/in @Thickness 0.125 in	ASTM D256

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.00e+15 ohm-cm	3.00e+15 ohm-cm	96 hours at 90°C; 50% RH; ASTM D257
	6.00e+15 ohm-cm	6.00e+15 ohm-cm	40 hours; 23C; 50% RH; ASTM D257
Dielectric Strength	24.0 kV/mm @Thickness 3.17 mm	610 kV/in @Thickness 0.125 in	ASTM D149
Arc Resistance	60 - 120 sec	60 - 120 sec	PLC 6
High Voltage Arc Resistance to Ignition (HVAR)	16 sec @Thickness 1.60 mm	16 sec @Thickness 0.0630 in	UL 746A
Comparative Tracking Index	250 - 400 V	250 - 400 V	PLC 2
Hot Wire Ignition, HWI	15 - 30 sec @Thickness 1.50 mm	15 - 30 sec @Thickness 0.0591 in	PLC 3
	30 - 60 sec @Thickness 3.00 mm	30 - 60 sec @Thickness 0.118 in	PLC 2
High Amp Arc Ignition, HAI	60 - 120 arcs @Thickness 3.00 mm	60 - 120 arcs @Thickness 0.118 in	PLC 1
	>= 120 arcs @Thickness 1.50 mm	>= 120 arcs @Thickness 0.0591 in	PLC 0
High Voltage Arc-Tracking Rate, HVTR	80.0 - 150 mm/min	3.15 - 5.91 in/min	PLC 3

Thermal Properties	Metric	English	Comments
CTE, linear	70.2 µm/m-°C @Temperature -40.0 - 95.0 °C	39.0 µin/in-°F @Temperature -40.0 - 203 °F	Flow; ASTM E831-06
CTE, linear, Transverse to Flow	68.4 µm/m-°C @Temperature -40.0 - 95.0 °C	38.0 µin/in-°F @Temperature -40.0 - 203 °F	ASTM E831-06
Deflection Temperature at 1.8 MPa (264 psi)	121 °C	250 °F	ASTM D648
	137 °C	279 °F	ISO 75
UL RTI, Electrical	125 °C	257 °F
UL RTI, Mechanical with Impact	115 °C	239 °F
UL RTI, Mechanical without Impact	125 °C	257 °F
Flammability, UL94	V-1 @Thickness 1.50 mm	V-1 @Thickness 0.0591 in
	V-0 @Thickness 3.00 mm	V-0 @Thickness 0.118 in
Oxygen Index	36.9 %	36.9 %	ASTM D2863
Glow Wire Test	960 °C	1760 °F	GWFI; IEC 695-2-1/2

Tristar® PC-10FR-(VIK) 16 MFI 以下型号敬请参考:

本公司还提供德国杜邦、美国首诺、美国PLA、日本UMG、基础创新塑料（美国）、美国舒尔曼、美国英威达、美国RTP、美国巴斯夫、上海巴斯夫、德国巴斯夫、马来西亚巴斯夫、日本东丽、日本三菱工程、德国朗盛、德国弗瑞圣塔、荷兰DSM、美国DSM、泰国杜邦、河南神马尼龙、三井TPX、意大利泰克尼卡、意大利兰蒂奇、意大利LATI、美国普立万、上海罗地亚、法国罗地亚、日本尤尼卡、深圳东丽、日本旭化成、日本东洋纺织、台湾南亚、惠州南亚、台湾新光、美国液氮、台湾太松、日本EMS、瑞士EMS、美国泰科纳、加拿大英威达、加拿大杜邦、新加坡杜邦、新加坡美乐、日本杜邦、等各种工程塑料.........

Tristar PC-06R 6.0 MFI Grade

Tristar PC-08 8 MFI Extrusion Grade

Tristar PC-10 10 MFI Extrusion Grade

Tristar PC-10FR 12 MFI Flame Retardant

Tristar PC-10FR-(16) 16 MFI Flame Retardant

Tristar PC-10FR-(18) 18 MFI Flame Retardant

Tristar PC-10FR-(8) 8 MFI Flame Retardant

Tristar PC-10FR-(V) 12 MFI Flame Retardant, UV te

Tristar PC-10FR-(V16) 16 MFI Flame Retardant

Tristar® PC-10FR-(V18) 18 MFI Flame Retardant, UV

Tristar PC-10FR-(VIM) 12 MFI Flame Retardant, UV

Tristar PC-10FR-(VIK) 16 MFI Flame Retardant, UV

Tristar PC-10FR-(V8) 8 MFI Flame Retardant, UV

Tristar PC-10FRNH 12 MFI Non-Bromine

Tristar PC-10FRNH-V 12 MFI Non-Bromine

Tristar PC-10FRN 15 MFI Flame Retardant

Tristar PC-10FRN (V) 15 MFI, 5VA, Flame

Tristar PC-10GFR 10% Glass Reinforced

Tristar PC-10GFR-(V) 10% Glass Reinforced UV

Tristar PC-10R 10 MFI Polycarbonate With Release

Tristar PC-10R-(14) 14 MFI Polycarbonate With Release
上海松翰塑化科技有限公司！本公司承诺，假一赔百！所有产品都是原厂家，原包装一线独家营销！可提供以下报告：COA（产地证明）SGS（检测报告） MSDS（成分报告） FDA（食品安全报告） UL黄卡(出口报告)正规17%的正规发票！欢迎新老客户来电咨询：

联系人：邓小姐

联系电话：13917657923

固定电话：021-51131842

联系QQ：996152797

联系信箱：996152797@qq.com