高分子聚合物；热凝；ABS；聚碳酸酯/ ABS合金、玻璃纤维填充聚碳酸酯（PC）；
颗粒 PC/ABS，聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物，是由聚碳酸酯（Polycarbonate）和聚丙烯精（ABS）合金而成的热可塑性塑胶，结合了两种材料的优异特性，ABS材料的成型性和PC的机械性、冲击强度和耐温、抗紫外线（UV）等性质，可广泛使用在汽车内部零件、事务机器、通信器材、家电用品及照明设备上。
| 参数： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.291 g/cc | 1.291 g/cc | ASTM D792 | ||
| Water Absorption | 0.15 % | 0.15 % | 24 hr. Immersion; ASTM D570 | ||
| Linear Mold Shrinkage | 0.0020 - 0.0025 cm/cm | 0.0020 - 0.0025 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 68.9 MPa | 10000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 6.21 GPa | 900 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 | ||
| Flexural Modulus | 6.21 GPa | 900 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.908 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.70 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 232 - 271 °C | 450 - 520 °F | Molding | ||
| Mold Temperature | >= 93.3 °C | >= 200 °F | |||
| Drying Temperature | 93.3 °C | 200 °F | |||
| Dry Time | 2 hour | 2 hour | |||
| De |
|||||
| Product Form | Pellets | ||||