类别：高分子聚合物；热凝；ABS；聚碳酸酯/ ABS合金，unreinforced聚碳酸酯（PC）；
材料说明：特点：
出色的平衡性能
良好的冲击强度
良好的加工性能
以下为电镀
应用：
注射成型
家用电器
汽车室内/外装饰配件
电信设备
计算机及配件
颗粒图| 参数： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.07 g/cc @Temperature 23.0 °C |
1.07 g/cc @Temperature 73.4 °F |
ASTM D792 | ||
| Water Absorption | 0.20 % @Temperature 23.0 °C, Time 86400 sec |
0.20 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Temperature 23.0 °C |
0.0050 - 0.0070 in/in @Temperature 73.4 °F |
Parallel; ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Temperature 23.0 °C |
0.0050 - 0.0070 in/in @Temperature 73.4 °F |
ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 108 | 108 | ASTM D785 | ||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 30 % | 30 % | 50mm/min; ASTM D638 | ||
| Flexural Strength | 80.0 MPa | 11600 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 2.30 GPa | 334 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | 3.43 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
6.43 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | ||
| Izod Impact, Unnotched | NB @Thickness 3.20 mm, Temperature 23.0 °C |
NB @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C @Thickness 6.40 mm |
221 °F @Thickness 0.252 in |
ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C @Thickness 6.40 mm |
194 °F @Thickness 0.252 in |
ASTM D648 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 250 °C | <= 482 °F | |||
| Rear Barrel Temperature | 210 - 230 °C | 410 - 446 °F | Start Point: 230°C | ||
| Middle Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 225°C | ||
| Front Barrel Temperature | 225 - 245 °C | 437 - 473 °F | Start Point: 230°C | ||
| Melt Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 230°C | ||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Start Point: 60°C | ||
| Drying Temperature | 90.0 - 100 °C @Time 14400 - 21600 sec |
194 - 212 °F @Time 4.00 - 6.00 hour |
Pre-dry | ||
| Back Pressure | 0.300 - 1.00 MPa | 43.5 - 145 psi | |||
| De |
|||||
| Injection Speed | 40-80% | ||||
| Weather Resistance (delta E) | ASTM D4459; 400hr xenon lamp | ||||