图类别：热塑性聚合物；聚合物；ABS；聚碳酸酯/ ABS合金，无筋；聚碳酸酯（PC）
图
图
材料注意事项：
特征：
无卤阻燃V-0 / 1.5mm，
出色的平衡性能
高耐热性
良好的耐化学性
良好的耐水解性
适用于涂料和电镀
下拉电阻
应用：
液晶电视，显示器，PDP
激光打印机，复印机
笔记本电脑和充电器
可充电电池
汽车dvd
电动工具充电器
电信设备
| 参数： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.20 g/cc @Temperature 23.0 °C |
1.20 g/cc @Temperature 73.4 °F |
ASTM D792 | ||
| Water Absorption | 0.12 % @Temperature 23.0 °C, Time 86400 sec |
0.12 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 | ||
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm @Temperature 23.0 °C |
0.0040 - 0.0060 in/in @Temperature 73.4 °F |
ASTM D955 | ||
| Melt Flow | 19 g/10 min @Load 5.00 kg, Temperature 260 °C |
19 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 120 | 120 | ASTM D785 | ||
| Tensile Strength at Break | 65.0 MPa | 9430 psi | 50mm/min; ASTM D638 | ||
| Elongation at Break | 50 % | 50 % | 50mm/min; ASTM D638 | ||
| Flexural Strength | 100 MPa | 14500 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 3.70 GPa | 537 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | 3.80 J/cm @Thickness 3.20 mm, Temperature -10.0 °C |
7.12 ft-lb/in @Thickness 0.126 in, Temperature 14.0 °F |
ASTM D256 | ||
| 8.00 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
15.0 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | |||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 | ||
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | 1.6mm; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C @Thickness 6.40 mm |
261 °F @Thickness 0.252 in |
ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C @Thickness 6.40 mm |
239 °F @Thickness 0.252 in |
ASTM D648 | ||
| Flammability, UL94 | 5VB @Thickness 1.60 mm |
5VB @Thickness 0.0630 in |
|||
| 5VA @Thickness 3.20 mm |
5VA @Thickness 0.126 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 265 °C | <= 509 °F | |||
| Rear Barrel Temperature | 230 - 255 °C | 446 - 491 °F | Start Point: 235°C | ||
| Middle Barrel Temperature | 230 - 260 °C | 446 - 500 °F | Start Point: 245°C | ||
| Front Barrel Temperature | 235 - 270 °C | 455 - 518 °F | Start Point: 255°C | ||
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | Start Point: 240°C | ||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Start Point: 60°C | ||
| Drying Temperature | 80.0 - 90.0 °C @Time 7200 - 14400 sec |
176 - 194 °F @Time 2.00 - 4.00 hour |
Pre-dry | ||
| Back Pressure | 0.300 - 0.700 MPa | 43.5 - 102 psi | |||
| De |
|||||
| Injection Speed | 50-80% | ||||