材料说明：描述：注塑，PC / ABS，火焰停留，防静电
应用：E和E（房屋）
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636 021 51131842
QQ ：205730283
邮 箱 ：205730283@qq.com
| 参数： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 11 g/10 min @Load 2.16 kg, Temperature 250 °C |
11 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 52.0 MPa @Thickness 3.20 mm |
7540 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | >= 50 % @Thickness 3.20 mm |
>= 50 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 85.3 MPa @Thickness 3.20 mm |
12400 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 2.45 GPa @Thickness 3.20 mm |
356 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | >= 4.90 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
>= 9.18 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C @Thickness 1.60 - 1.70 mm |
140 °F @Thickness 0.0630 - 0.0669 in |
|
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness 1.60 - 1.70 mm |
140 °F @Thickness 0.0630 - 0.0669 in |
|
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness 1.60 - 1.70 mm |
140 °F @Thickness 0.0630 - 0.0669 in |
|
| Flammability, UL94 | V-2 @Thickness 1.60 - 1.70 mm |
V-2 @Thickness 0.0630 - 0.0669 in |
|
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 210 - 240 °C | 410 - 464 °F | Injection Molding |
| Middle Barrel Temperature | 215 - 250 °C | 419 - 482 °F | Injection Molding |
| Front Barrel Temperature | 225 - 260 °C | 437 - 500 °F | Injection Molding |
| Nozzle Temperature | 220 - 250 °C | 428 - 482 °F | Injection Molding |
| Melt Temperature | 230 - 260 °C | 446 - 500 °F | Injection Molding |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | Injection Molding |
| Drying Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |