LG GP5006AF PC/ABS 阻燃 PC/ABS的综合性能优良，但是其耐化学品性能差而容易受到比较强的化学溶剂侵蚀而导致制品开裂等缺陷。特别是当PC/ABS 制品喷涂某些车身外饰漆时，由于其溶剂的强腐蚀性，易导致制品出现应力痕，龟裂，甚至开裂。

PC/ABS，聚碳酸酯和丙烯腈-丁二烯-苯乙烯共聚物和混合物，是由聚碳酸酯（Polycarbonate）和聚丙烯腈（ABS）合金而成的热可塑性塑胶，结合了两种材料的优异特性，ABS材料的成型性和PC的机械性、冲击强度和耐温、抗紫外线（UV）等性质，可广泛使用在汽车内部零件、事务机器、通信器材、家电用品及照明设备上。
典型应用范围:
汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件　2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器　3.电信，移动电话外壳，附件以及智能卡（SIM卡）：　4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道　5.家用电器，如洗衣机，吹风机，微波炉内外部件等。

Physical Properties	Metric	English	Comments
物性表：
Specific Gravity	1.17 g/cc	1.17 g/cc	ASTM D792
Maximum Moisture Content	0.020	0.020	Injection Molding
Linear Mold Shrinkage, Flow	0.0050 - 0.0080 cm/cm @Thickness 3.20 mm	0.0050 - 0.0080 in/in @Thickness 0.126 in	ASTM D955
Melt Flow	6.0 g/10 min @Load 2.16 kg, Temperature 250 °C	6.0 g/10 min @Load 4.76 lb, Temperature 482 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	108	108	ASTM D785
Tensile Strength, Yield	51.0 MPa @Thickness 3.20 mm	7400 psi @Thickness 0.126 in	50mm/min; ASTM D638
Elongation at Break	60 % @Thickness 3.20 mm	60 % @Thickness 0.126 in	50mm/min; ASTM D638
Flexural Yield Strength	78.5 MPa @Thickness 3.20 mm	11400 psi @Thickness 0.126 in	10mm/min; ASTM D790
Flexural Modulus	2.16 GPa @Thickness 3.20 mm	313 ksi @Thickness 0.126 in	10mm/min; ASTM D790
Izod Impact, Notched	4.41 J/cm @Thickness 3.20 mm, Temperature 23.0 °C	8.27 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	104 °C @Thickness 6.40 mm	219 °F @Thickness 0.252 in	Unannealed; ASTM D648
UL RTI, Electrical	85.0 °C @Thickness >=0.750 mm	185 °F @Thickness >=0.0295 in
	85.0 °C @Thickness >=1.70 mm	185 °F @Thickness >=0.0669 in
	85.0 °C @Thickness >=3.00 mm	185 °F @Thickness >=0.118 in
UL RTI, Mechanical with Impact	75.0 °C @Thickness >=0.750 mm	167 °F @Thickness >=0.0295 in
	75.0 °C @Thickness >=1.70 mm	167 °F @Thickness >=0.0669 in
	75.0 °C @Thickness >=3.00 mm	167 °F @Thickness >=0.118 in
UL RTI, Mechanical without Impact	75.0 °C @Thickness >=0.750 mm	167 °F @Thickness >=0.0295 in
	75.0 °C @Thickness >=1.70 mm	167 °F @Thickness >=0.0669 in
	75.0 °C @Thickness >=3.00 mm	167 °F @Thickness >=0.118 in
Flammability, UL94	V-0 @Thickness >=0.750 mm	V-0 @Thickness >=0.0295 in
	V-0 @Thickness >=1.70 mm	V-0 @Thickness >=0.0669 in
	5VB @Thickness >=3.00 mm	5VB @Thickness >=0.118 in

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	240 - 270 °C	464 - 518 °F	Injection Molding
Middle Barrel Temperature	245 - 275 °C	473 - 527 °F	Injection Molding
Front Barrel Temperature	245 - 275 °C	473 - 527 °F	Injection Molding
Nozzle Temperature	245 - 275 °C	473 - 527 °F	Injection Molding
Melt Temperature	240 - 270 °C	464 - 518 °F	Injection Molding
Mold Temperature	50.0 - 70.0 °C	122 - 158 °F	Injection Molding
Drying Temperature	80.0 - 100 °C	176 - 212 °F	Injection Molding
Dry Time	4.00 - 6.00 hour	4.00 - 6.00 hour	Injection Molding
Back Pressure	0.981 - 3.92 MPa	142 - 569 psi	Injection Molding
Screw Speed	40 - 70 rpm	40 - 70 rpm	Injection Molding