材料：PC优越的强度和耐热性能和ABS的灵活性。PC-ABS共混物中常用的汽车，
应用电子电信。零件建模PC-ABS功能成型技术理想，制造的，
工具和终端使用的部分。
图
图| Thermal Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| CTE, linear | 72.0 µm/m-°C @Temperature -40.0 - 35.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 95.0 °F |
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 | ||
| Flammability, UL94 | HB | HB | 3.18 mm (1/8") (MRC Rating) | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 260 - 282 °C | 500 - 540 °F | |||
| Rear Barrel Temperature | 249 - 271 °C | 480 - 520 °F | |||
| Middle Barrel Temperature | 260 - 277 °C | 500 - 531 °F | |||
| Front Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |||
| Nozzle Temperature | 260 - 282 °C | 500 - 540 °F | |||
| Mold Temperature | 49.0 - 82.0 °C | 120 - 180 °F | |||
| Drying Temperature | 110 °C | 230 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Dew Point | <= -17.8 °C | <= 0.000 °F | |||
| Drying Air Flow Rate | 22.7 - 28.3 l/min | 0.800 - 1.00 ft³/min (CFM) | per lb/hour resin processed | ||
| Injection Pressure | 68.9 - 138 MPa | 10000 - 20000 psi | |||
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |||
| Cushion | 0.330 - 0.635 cm | 0.130 - 0.250 in | |||
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | |||
| De |
|||||
| Fill Rate | Slow - Moderate | ||||
| Hold Pressure | 40 - 60% of injection pressure | ||||
| Packing Pressure | 50 - 75% of injection pressure |
||||