特点：
1、综合性能较好，冲击强度较高，化学稳定性，电性能良好.
2、与372有机玻璃的熔接性良好，制成双色塑件，且可表面镀铬，喷漆处理.
3、有高抗冲、高耐热、阻燃、增强、透明等级别。
4、流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。
5、用途：适于制作一般机械零件，减磨耐磨零件，传动零件和电讯零件.
6、同PVC（聚氯乙烯）一样在屈折处会出现白化现象。
典型应用范围:
汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件 2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器 3.电信，移动电话外壳，附件以及智能卡（SIM卡）： 4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道 5.家用电器，如洗衣机，吹风机，微波炉内外部件等。
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | |||
| Thickness | 406 microns | 16.0 mil | |||
| Linear Mold Shrinkage | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | 4 mm thick, 10.0 mm wide molded rod; ISO 294-4 | ||
| Melt Flow | 0.50 g/10 min @Load 5.00 kg, Temperature 240 °C |
0.50 g/10 min @Load 11.0 lb, Temperature 464 °F |
ISO 1133 | ||
| 1.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
1.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ISO 1133 | |||
| High Load Melt Index | 18 g/10 min @Load 21.6 kg, Temperature 240 °C |
18 g/10 min @Load 47.6 lb, Temperature 464 °F |
ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 37.0 MPa | 5370 psi | ISO 527 | ||
| Film Elongation at Break, MD | 20 % | 20 % | ISO 527 | ||
| Film Elongation at Yield, MD | 5.0 % | 5.0 % | ISO 527 | ||
| Modulus of Elasticity | 2.70 GPa | 392 ksi | 4 mm thick;10.0 mm wide molded rod; ISO 178 | ||
| Izod Impact, Notched | 0.300 J/cm @Thickness 4.00 mm, Temperature -20.0 °C |
0.562 ft-lb/in @Thickness 0.157 in, Temperature -4.00 °F |
ISO 180 | ||
| 2.30 J/cm @Thickness 4.00 mm, Temperature 23.0 °C |
4.31 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F |
ISO 180 | |||
| Izod Impact, Unnotched | 2.70 J/cm @Thickness 4.00 mm, Temperature 23.0 °C |
5.06 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F |
ISO 180 | ||
| 5.00 J/cm @Thickness 4.00 mm, Temperature -20.0 °C |
9.37 ft-lb/in @Thickness 0.157 in, Temperature -4.00 °F |
ISO 180 | |||
| Film Tensile Strength at Break, MD | 35.0 MPa | 5080 psi | ISO 527 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 1000 ohm-cm | <= 1000 ohm-cm | 400 um thick sheet; ISO D-257 | ||
| Surface Resistance | <= 100000 ohm | <= 100000 ohm | 400 um thick sheet; ISO D-257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C | 232 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Bf | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C | 207 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Af | ||
| Vicat Softening Point | 118 °C | 244 °F | Rate B; 4 mm thick;10.0 mm wide molded rod; ISO 306/B50 | ||
| 138 °C | 280 °F | Rate A; 4 mm thick;10.0 mm wide molded rod; ISO 306/A50 | |||
| Processing Properties | Metric | English | Comments | ||
| Middle Barrel Temperature | 280 °C | 536 °F | Zone 1; Cylinder | ||
| 290 °C | 554 °F | Zone 2; Cylinder | |||
| 290 °C | 554 °F | Zone 3; Cylinder | |||
| 290 °C | 554 °F | Zone 4; Cylinder | |||
| 300 °C | 572 °F | Zone 5; Cylinder | |||
| 300 °C | 572 °F | Zone 6; Cylinder | |||
| Die Temperature | 290 °C | 554 °F | Zone 3 | ||
| 300 °C | 572 °F | Zone 1 | |||
| 300 °C | 572 °F | Zone 4 | |||
| 300 °C | 572 °F | Zone 5 | |||
| 300 °C | 572 °F | Zone 2 | |||
| Roll Temperature | 70.0 °C | 158 °F | 3rd Roll | ||
| 80.0 °C | 176 °F | 2nd Roll | |||
| 90.0 °C | 194 °F | 1st Roll | |||
| Drying Temperature | 120 °C @Time 10800 - 14400 sec |
248 °F @Time 3.00 - 4.00 hour |
Pre-drying in a dehumidifier | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | When Produced | ||
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions | ||
| De |
|||||
| Appearance | Granule | ||||
| Color | Black | ||||