特点：
1、综合性能较好，冲击强度较高，化学稳定性，电性能良好.
2、与372有机玻璃的熔接性良好，制成双色塑件，且可表面镀铬，喷漆处理.
3、有高抗冲、高耐热、阻燃、增强、透明等级别。
4、流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。
5、用途：适于制作一般机械零件，减磨耐磨零件，传动零件和电讯零件.
6、同PVC（聚氯乙烯）一样在屈折处会出现白化现象。
典型应用范围:
汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件 2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器 3.电信，移动电话外壳，附件以及智能卡（SIM卡）： 4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道 5.家用电器，如洗衣机，吹风机，微波炉内外部件等。
| 物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D792 | ||
| Density | 1.25 g/cc | 0.0452 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ASTM D570 | ||
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 | ||
| 0.0100 % | 0.0100 % | 23°C / 50% RH; ISO 62 | |||
| Water Absorption at Saturation | 0.090 % | 0.090 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method | ||
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method | ||
| Melt Flow | 17.5 g/10 min @Load 2.16 kg, Temperature 260 °C |
17.5 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 | ||
| Melt Index of Compound | 14 g/10 min @Load 5.00 kg, Temperature 220 °C |
14 g/10 min @Load 11.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D638 | ||
| 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 | |||
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 | ||
| 65.0 MPa | 9430 psi | Type I, 5 mm/min; ASTM D638 | |||
| Elongation at Break | 15 % | 15 % | 50 mm/min; ISO 527 | ||
| 100 % | 100 % | Type I, 5 mm/min; ASTM D638 | |||
| Elongation at Yield | 3.5 % | 3.5 % | 5 mm/min; ISO 527 | ||
| 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 | |||
| Tensile Modulus | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 | ||
| 3.50 GPa | 508 ksi | 5 mm/min; ASTM D638 | |||
| Flexural Yield Strength | 97.0 MPa | 14100 psi | 2 mm/min; ISO 178 | ||
| 100 MPa | 14500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |||
| Flexural Modulus | 3.30 GPa | 479 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| 3.45 GPa | 500 ksi | 2 mm/min; ISO 178 | |||
| Izod Impact, Notched | 2.00 J/cm | 3.75 ft-lb/in | ASTM D256 | ||
| 0.880 J/cm @Temperature -30.0 °C |
1.65 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*3; ISO 180/1A | ||
| 5.00 kJ/m² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA | ||
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |||
| Dart Drop, Total Energy | 50.0 J @Temperature 23.0 °C |
36.9 ft-lb @Temperature 73.4 °F |
ASTM D3763 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.68e+16 ohm-cm | 2.68e+16 ohm-cm | ASTM D257 | ||
| Surface Resistance | 3.54e+15 ohm | 3.54e+15 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 55.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.6 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | ||
| 55.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
30.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |||
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | ||
| 60.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
33.3 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C @Thickness 6.40 mm |
207 °F @Thickness 0.252 in |
unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
| 83.0 °C @Thickness 3.20 mm |
181 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |||
| 89.0 °C @Thickness 6.40 mm |
192 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |||
| Vicat Softening Point | 91.0 °C | 196 °F | Rate B/50; ASTM D1525 | ||
| 98.0 °C | 208 °F | Rate B/50; ISO 306 | |||
| 102 °C | 216 °F | Rate B/120; ISO 306 | |||
| Flammability, UL94 | V-1 @Thickness 0.600 mm |
V-1 @Thickness 0.0236 in |
UL 94 | ||
| V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 | |||
| 5VB @Thickness 1.50 mm |
5VB @Thickness 0.0591 in |
UL 94 | |||
| Glow Wire Test | 800 °C | 1470 °F | IEC 60695-2-13 | ||
| 850 °C | 1560 °F | IEC 60695-2-13 | |||
| 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
IEC 60695-2-12 | |||
| De |
|||||
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |
|||