特点：
1、综合性能较好，冲击强度较高，化学稳定性，电性能良好.
2、与372有机玻璃的熔接性良好，制成双色塑件，且可表面镀铬，喷漆处理.
3、有高抗冲、高耐热、阻燃、增强、透明等级别。
4、流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。
5、用途：适于制作一般机械零件，减磨耐磨零件，传动零件和电讯零件.
6、同PVC（聚氯乙烯）一样在屈折处会出现白化现象。
典型应用范围:
汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件 2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器 3.电信，移动电话外壳，附件以及智能卡（SIM卡）： 4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道 5.家用电器，如洗衣机，吹风机，微波炉内外部件等。
| 物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.60 % | 0.60 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method | ||
| Melt Index of Compound | 23 g/10 min @Load 2.16 kg, Temperature 260 °C |
23 g/10 min @Load 4.76 lb, Temperature 500 °F |
MVR [cm^3/10 min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 50 mm/min; ISO 527 | ||
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |||
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | Type I, 50 mm/min; ASTM D638 | ||
| 63.0 MPa | 9140 psi | 50 mm/min; ISO 527 | |||
| Elongation at Break | 35 % | 35 % | 50 mm/min; ISO 527 | ||
| 65 % | 65 % | Type I, 50 mm/min; ASTM D638 | |||
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 | ||
| 4.1 % | 4.1 % | Type I, 50 mm/min; ASTM D638 | |||
| Tensile Modulus | 2.75 GPa | 399 ksi | 1 mm/min; ISO 527 | ||
| 2.76 GPa | 400 ksi | 5 mm/min; ASTM D638 | |||
| Flexural Yield Strength | 94.0 MPa | 13600 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 2.44 GPa | 354 ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Notched | 4.75 J/cm | 8.90 ft-lb/in | ASTM D256 | ||
| 1.00 J/cm @Temperature -30.0 °C |
1.87 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |||
| Izod Impact, Notched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1A | ||
| 45.0 kJ/m² | 21.4 ft-lb/in² | 80*10*3; ISO 180/1A | |||
| 10.0 kJ/m² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A | |||
| 12.0 kJ/m² @Temperature -30.0 °C |
5.71 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |||
| Charpy Impact, Notched | 3.30 J/cm² | 15.7 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| 4.50 J/cm² | 21.4 ft-lb/in² | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |||
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ROA; IEC 60093 | ||
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 2.9 @Frequency 50.0 - 60.0 Hz |
2.9 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |||
| Dielectric Strength | 31.0 kV/mm @Thickness 1.60 mm |
787 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | ||
| 46.0 kV/mm @Thickness 0.800 mm |
1170 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |||
| Dissipation Factor | 0.0020 @Frequency 50.0 - 60.0 Hz |
0.0020 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | ||
| 0.0070 @Frequency 1.00e+6 Hz |
0.0070 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A | ||
| Hot Wire Ignition, HWI | 15 - 30 sec | 15 - 30 sec | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
| Vicat Softening Point | 104 °C | 219 °F | Rate B/50; ISO 306 | ||
| 106 °C | 223 °F | Rate B/120; ISO 306 | |||
| UL RTI, Electrical | 85.0 °C | 185 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 85.0 °C | 185 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 85.0 °C | 185 °F | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 | ||
| 5VB @Thickness 2.50 mm |
5VB @Thickness 0.0984 in |
UL 94 | |||
| Oxygen Index | 31 % | 31 % | ISO 4589 | ||
| Glow Wire Test | 825 °C | 1520 °F | IEC 60695-2-13 | ||
| 825 °C | 1520 °F | IEC 60695-2-13 | |||
| 825 °C | 1520 °F | IEC 60695-2-13 | |||
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
IEC 60695-2-12 | |||
| De |
|||||
| Ball Pressure Test, 75°C +/- 2°C | PASS | IEC 60695-10-2 |
|||