TPU 70 H 4673 M 良好的熔体流动/高弹性==_产品资讯

TPU 70 H 4673 M 拥有良好的抗撕裂强度及延伸性/可耐低温曲折/耐冲击性，耐磨性特别突出/耐油脂/耐老性/高度防水/良好机械性/耐寒性===
QQ截图20150512204113

颗粒图片

原料加工产品展示
TPU 70 H 4673 M 物性表：

Physical Properties	Metric	English	Comments
Density	1.15 g/cc	0.0415 lb/in³	ASTM D792
Linear Mold Shrinkage	0.0090 cm/cm	0.0090 in/in	ASTM D995
Melt Index of Compound	45 g/10 min @Load 5.00 kg, Temperature 190 °C	45 g/10 min @Load 11.0 lb, Temperature 374 °F	cm³/10 min

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	71	71	ASTM D2240
Hardness, Shore D	21	21	ASTM D2240
Tensile Strength at Break	35.0 MPa	5080 psi	DIN 53504
Elongation at Break	880 %	880 %	DIN 53504
100% Modulus	0.00340 GPa	0.493 ksi	DIN 53504
300% Modulus	0.00700 GPa	1.02 ksi	DIN 53504
Tear Strength	45.1 kN/m	257 pli	DIN 53515
Abrasion	35	35	[mm³]; ISO 4649
Compression Set	34 % @Temperature 23.0 °C, Time 252000 sec	34 % @Temperature 73.4 °F, Time 70.0 hour	ASTM D395
	48 % @Temperature 70.0 °C, Time 86400 sec	48 % @Temperature 158 °F, Time 24.0 hour	ASTM D395

Processing Properties	Metric	English	Comments
Feed Temperature	175 °C	347 °F	Injection
Front Barrel Temperature	180 °C	356 °F	Injection
Adapter Temperature	180 °C	356 °F	Injection
Die Temperature	170 °C	338 °F	Injection
Melt Temperature	145 - 170 °C	293 - 338 °F

Descriptive Properties
TMA High	165°C
TMA Low	120°C

物性优势：

高耐磨性:硬度范围广：通过改变/TPU各反应组分的配比，可以得到不同硬度的产品，而且随着硬度的增加,其产品仍保持良好的弹性/机械强度高：制品的承载能力、抗冲击性及减震性能突出、耐寒性突出：TPU的玻璃态转变温度比较低，在零下35度仍保持良好的弹性、柔顺性和其他物理性能、加工性能好、TPU可采用常见的热塑性材料的加工方法进行加工，

可采用常见的热塑性材料的加工方法进行加工,如注射、挤出、压延等等、同时，TPU与某些高分子材料共同加工能够得到性能互补的聚合物合金、耐油、耐水、耐霉菌、在生利用性好。

应用领域：

　1.鞋类：运动鞋Logo、运动鞋气垫、登山鞋、雪鞋、高尔夫球鞋、溜冰鞋、之面料及内里贴合材料。

　2.成衣类：雪衣、雨衣、风衣、防寒夹克、野战服、纸尿裤、生理裤、等面料复合材料(防水透湿)。

　3医药类：手术衣、帽、鞋、医院用褥垫、冰袋、绷带、血浆袋、外科用包扎布条、口罩、等面料及内里材料，手术床气囊。

　4国防用品：飞机油箱，武器封存覆膜、帐棚窗口、军用水袋、救生衣，充汽艇等之面料及内里面料，气囊。

　5.运动用品：足球表面及内胆、充气床、饮水袋、滑雪手套(防水袋)、潜水衣、雪衣、泳装、滑雪板、商标、气囊、运动衫、瘦身衣等面料及内里材料。