TPU 85 E 4993 物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D995 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 85 | 85 | ASTM D2240 |
| Hardness, Shore D | 35 | 35 | ASTM D2240 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | DIN 53504 |
| Elongation at Break | 800 % | 800 % | ASTM D412 |
| 100% Modulus | 0.00550 GPa | 0.798 ksi | DIN 53504 |
| 300% Modulus | 0.0126 GPa | 1.83 ksi | DIN 53504 |
| Rebound | 36 % | 36 % | Bayshore; ASTM D2632 |
| Tear Strength | 105 kN/m | 600 pli | ASTM D624 |
| Abrasion | 30 | 30 | [mm3]; ISO 4649 |
| Compression Set | 19 % @Temperature 23.0 °C, Time 252000 sec |
19 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 36 % @Temperature 70.0 °C, Time 86400 sec |
36 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 | |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 5.00e+8 ohm | 5.00e+8 ohm | antistat |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 - 175 °C | 329 - 347 °F |
|
高耐磨性:硬度范围广：通过改变/TPU各反应组分的配比，可以得到不同硬度的产品，而且随着硬度的增加,其产品仍保持良好的弹性/机械强度高：制品的承载能力、抗冲击性及减震性能突出、耐寒性突出：TPU的玻璃态转变温度比较低，在零下35度仍保持良好的弹性、柔顺性和其他物理性能、加工性能好、TPU可采用常见的热塑性材料的加工方法进行加工，
可采用常见的热塑性材料的加工方法进行加工,如注射、挤出、压延等等、同时，TPU与某些高分子材料共同加工能够得到性能互补的聚合物合金、耐油、耐水、耐霉菌、在生利用性好。
应用领域：
1.鞋类：运动鞋Logo、运动鞋气垫、登山鞋、雪鞋、高尔夫球鞋、溜冰鞋、之面料及内里贴合材料。
2.成衣类：雪衣、雨衣、风衣、防寒夹克、野战服、纸尿裤、 生理裤、等面料复合材料(防水透湿)。
3医药类：手术衣、帽、鞋、 医院用褥垫、冰袋、绷带、血浆袋、外科用包扎布条、口罩、等面料及内里材料，手术床气囊。
4国防用品：飞机油箱，武器封存覆膜、帐棚窗口、军用水袋、救生衣，充汽艇等之面料及内里面料，气囊。
5.运动用品：足球表面及内胆、充气床、饮水袋、滑雪手套(防水袋)、潜水衣、雪衣、泳装、滑雪板、商标、气囊、运动衫、瘦身衣等面料及内里材料。
上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询