特点：
1、综合性能较好，冲击强度较高，化学稳定性，电性能良好.
2、与372有机玻璃的熔接性良好，制成双色塑件，且可表面镀铬，喷漆处理.
3、有高抗冲、高耐热、阻燃、增强、透明等级别。
4、流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。
5、用途：适于制作一般机械零件，减磨耐磨零件，传动零件和电讯零件.
6、同PVC（聚氯乙烯）一样在屈折处会出现白化现象。
典型应用范围:
汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件 2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器 3.电信，移动电话外壳，附件以及智能卡（SIM卡）： 4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道 5.家用电器，如洗衣机，吹风机，微波炉内外部件等。
| 物性表： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| 31 g/10 min @Load 10.0 kg, Temperature 250 °C |
31 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength at Break | 39.2 MPa | 5690 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 49.0 MPa | 7110 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.91 GPa | 277 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 65.7 MPa | 9530 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.91 GPa | 277 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 2.45 J/cm @Thickness 6.35 mm, Temperature -30.0 °C |
4.59 ft-lb/in @Thickness 0.250 in, Temperature -22.0 °F |
ASTM D256 |
| 3.92 J/cm @Thickness 3.17 mm, Temperature -30.0 °C |
7.35 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F |
ASTM D256 | |
| 4.12 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
7.71 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
ASTM D256 | |
| 5.39 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
10.1 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C @Thickness 6.40 mm |
212 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 111 °C | 232 °F | B/50; ISO R306 |