TPU 58070 物性表：
个别产品成品图片
TPU 58070 物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 72 @Time 5.00 sec |
72 @Time 0.00139 hour |
ASTM D2240 |
| Tensile Strength | 45.0 MPa | 6530 psi | ASTM D412 |
| 39.6 MPa @Temperature 25.0 °C, Time 2.42e+6 sec |
5740 psi @Temperature 77.0 °F, Time 672 hour |
ASTM Fuel B; ASTM D412 | |
| 45.0 MPa @Temperature 136 °C, Time 605000 sec |
6530 psi @Temperature 277 °F, Time 168 hour |
Air Oven; ASTM D412 | |
| 45.0 MPa @Temperature 25.0 °C, Time 2.42e+6 sec |
6530 psi @Temperature 77.0 °F, Time 672 hour |
ASTM Fuel A; ASTM D412 | |
| Tensile Strength, Yield | 600 MPa | 87000 psi | 100% elongation; ASTM D412 |
| 900 MPa | 131000 psi | 300% elongation; ASTM D412 | |
| Elongation at Break | 700 % | 700 % | Ultimate; ASTM D412 |
| 630 % @Temperature 136 °C, Time 605000 sec |
630 % @Temperature 277 °F, Time 168 hour |
Air Oven; ASTM D412 | |
| 700 % @Temperature 25.0 °C, Time 2.42e+6 sec |
700 % @Temperature 77.0 °F, Time 672 hour |
ASTM Fuel A; ASTM D412 | |
| 700 % @Temperature 25.0 °C, Time 2.42e+6 sec |
700 % @Temperature 77.0 °F, Time 672 hour |
ASTM Fuel B; ASTM D412 | |
| Tensile Modulus | 0.00260 GPa @Temperature 25.0 °C |
0.377 ksi @Temperature 77.0 °F |
Gehman Rigidity; ASTM D1053 |
| 0.00310 GPa @Temperature -20.0 °C |
0.450 ksi @Temperature -4.00 °F |
Gehman Rigidity; ASTM D1053 | |
| 0.00370 GPa @Temperature -30.0 °C |
0.537 ksi @Temperature -22.0 °F |
Gehman Rigidity; ASTM D1053 | |
| 0.00700 GPa @Temperature -40.0 °C |
1.02 ksi @Temperature -40.0 °F |
Gehman Rigidity; ASTM D1053 | |
| 0.0917 GPa @Temperature -50.0 °C |
13.3 ksi @Temperature -58.0 °F |
Gehman Rigidity; ASTM D1053 | |
| Tear Strength | 17.5 kN/m | 100 pli | Trouser; ASTM D470 |
| Graves Tear Strength | 78.9 kN/m | 450 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 50 | 50 | H18; ASTM D3389 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 165 °C | 329 °F | DSC |
| Glass Transition Temp, Tg | -52.0 °C | -61.6 °F | DSC |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 175 °C | 347 °F | Injection |
| Middle Barrel Temperature | 180 °C | 356 °F | Injection |
| Front Barrel Temperature | 195 °C | 383 °F | Injection |
| Nozzle Temperature | 200 °C | 392 °F | Injection |
| Zone 1 | 165 °C | 329 °F | Extrusion |
| Zone 2 | 170 °C | 338 °F | Extrusion |
| Zone 3 | 175 °C | 347 °F | Extrusion |
| Zone 4 | 180 °C | 356 °F | Extrusion |
| Adapter Temperature | 180 °C | 356 °F | 5, Extrusion |
| Die Temperature | 180 °C | 356 °F | 6, Zone 1, Extrusion |
| 180 °C | 356 °F | Zone 2, Extrusion | |
| Melt Temperature | 200 °C | 392 °F | Injection |
| Drying Temperature | 82.0 °C | 180 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Dew Point | -40.0 °C | -40.0 °F | |
| Injection Pressure | 34.5 - 68.9 MPa | 5000 - 10000 psi | Injection |
| Hold Pressure | 13.8 - 55.2 MPa | 2000 - 8000 psi | Injection |
| Back Pressure | 0.000 - 6.89 MPa | 0.000 - 1000 psi | Injection |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm | Injection |
应用介绍：
1．薄膜和片材（TPU具较好耐磨性、抗刺穿性、抗撕裂性、弹性、粘合性）（TPU薄膜应用在冬季服装、鞋类具有防寒、保暖、防水性能好等特性外还具有特别好的透气性）
2．管材（TPU具有高伸长率，良好耐水解和抗微生物性、耐油性、优异机械性能，如作消防水管内衬，输油管气动软管等）
3．鞋底，鞋邦等鞋材料（TPU具有突出耐磨性、抗刮性、耐刺穿性、抗纵向弯曲强度和低温冲击强度，其耐撕裂性和抗裂纹传播性是所有塑料中最好的。如作溜冰、滑雪靴、运动鞋、特种功能鞋等）
4．电线、电缆、光缆护套（TPU具良好耐磨性、耐环境、耐候性、耐腐蚀性、绝缘性、弹性和低温柔韧性等）
5．拉链片、高档塑料表带、表壳以及潜水表、礼品表等系列（TPU具有高弹、耐折、耐水性好手感舒适等）
6．机械制品和其它应用（如制造汽车部件、机械轴承、滚轮、输送带、橡塑筛网、工业胶管,垫圈,密封圈,游泳镜,冲浪板,表带,动物标牌,电器零部件,涂料,粘合剂,纤维等.)
上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询