颗粒图片
个别产品应用展示图
TTPV 4145 物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in³ | ASTM D792 |
| Viscosity | 318000 cP @Shear Rate 206 1/s, Temperature 200 °C |
318000 cP @Shear Rate 206 1/s, Temperature 392 °F |
ASTM D3835 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 45 | 45 | extruded sample; 5 sec. delay; ASTM D2240 |
| 48 | 48 | injection molded sample; 5 sec. delay; ASTM D2240 | |
| Tensile Strength at Break | 2.70 MPa | 392 psi | Die C; Flow direction; ASTM D412 |
| 4.00 MPa | 580 psi | Die C; Cross direction; ASTM D412 | |
| Elongation at Break | 243 % | 243 % | Die C; Flow direction; ASTM D412 |
| 429 % | 429 % | Die C; Cross direction; ASTM D412 | |
| 100% Modulus | 0.00130 GPa | 0.189 ksi | Die C; Cross direction; ASTM D412 |
| 0.00170 GPa | 0.247 ksi | Die C; Flow direction; ASTM D412 | |
| Tear Strength | 20.0 kN/m | 114 pli | Die C; Cross direction; ASTM D624 |
| Compression Set | 11 % | 11 % | 22h/23°C; ASTM D395B |
 |
35 % @Temperature 100 °C |
35 % @Temperature 212 °F |
22hr; ASTM D395B |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 182 - 204 °C | 360 - 400 °F | Extrusion |
| 177 - 216 °C | 350 - 420 °F | Injection Molding | |
| Middle Barrel Temperature | 182 - 204 °C | 360 - 400 °F | Extrusion Transition Zone |
| 177 - 216 °C | 350 - 420 °F | Injection Molding | |
| 188 - 210 °C | 370 - 410 °F | Extrusion Metering Zone | |
| Front Barrel Temperature | 177 - 216 °C | 350 - 420 °F | Injection Molding |
| 188 - 210 °C | 370 - 410 °F | Extrusion | |
| Nozzle Temperature | 188 - 221 °C | 370 - 430 °F | Injection Molding |
| Die Temperature | 193 - 216 °C | 380 - 420 °F | Extrusion |
| Melt Temperature | 182 - 221 °C | 360 - 430 °F | Injection Molding |
| 193 - 216 °C | 380 - 420 °F | Extrusion | |
| Mold Temperature | 10.0 - 65.6 °C | 50.0 - 150 °F | Injection Molding |
| Roll Temperature | 21.1 - 48.9 °C | 70.0 - 120 °F | Extrusion |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 hour | 3 hour | |
| Injection Pressure | 0.0689 - 1.03 MPa | 10.0 - 150 psi | Injection Molding Back Pressure |
| Screw Speed | 100 - 200 rpm | 100 - 200 rpm | Injection Molding |
1、 优异的抗老化性能和良好的耐候、耐热性能；
2、 优异的抗永久变形性能；
3、 优异的抗张强度、高韧性和高回弹性；
4、 优异的环保性能和可重复使用；
5、 优异的电绝缘性能；
6、 硬度范围广泛；
7、 使用温度范围广泛；
8、 颜色多样化，有全透明、半透明、浅色系列，着色容易，容易加工成型；
9、 可与PP、PA、PC、ABS、PS、PBT、PET等多种材料共注射或挤出成型。
广泛应用于：电子产品外壳及外保护、建筑材料密封条、交通器材缓冲部件、消费品的主体如鱼竿牙刷吸管、各种管道管件等、、、、
上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询