特点：
1、综合性能较好，冲击强度较高，化学稳定性，电性能良好.
2、与372有机玻璃的熔接性良好，制成双色塑件，且可表面镀铬，喷漆处理.
3、有高抗冲、高耐热、阻燃、增强、透明等级别。
4、流动性比HIPS差一点，比PMMA、PC等好，柔韧性好。
5、用途：适于制作一般机械零件，减磨耐磨零件，传动零件和电讯零件.
6、同PVC（聚氯乙烯）一样在屈折处会出现白化现象。
典型应用范围:
汽车内外饰：仪表板，饰柱，仪表前盖，格栅，内外饰件 2.商务设备机壳和内置部件：笔记本/台式电脑，复印机，打印机，绘图仪，显示器 3.电信，移动电话外壳，附件以及智能卡（SIM卡）： 4.电器产品，电子产品外壳，电表罩和壳体，家用开关，插头和插座，电缆电线管道 5.家用电器，如洗衣机，吹风机，微波炉内外部件等。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
| General Information | ||||
| General | ||||
|
Material Status
|
|
|||
|
Availability
|
|
|||
|
Features
|
|
|||
|
Uses
|
|
|||
|
Appearance
|
|
|||
|
Processing Method
|
|
|||
| ASTM & ISO Properties 1 | |||
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.21
|
g/cm³
|
ASTM D792 |
|
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg)
|
13
|
g/10 min
|
ASTM D1238 |
|
Molding Shrinkage - Flow (3.20 mm)
|
0.40 to 0.60
|
%
|
ASTM D955 |
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength 2 (Yield, 3.20 mm)
|
72.6
|
MPa
|
ASTM D638 |
|
Tensile Elongation 2 (Break, 3.20 mm)
|
> 50
|
%
|
ASTM D638 |
|
Flexural Modulus 3 (3.20 mm)
|
2650
|
MPa
|
ASTM D790 |
|
Flexural Strength 3 (3.20 mm)
|
118
|
MPa
|
ASTM D790 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (23°C, 3.20 mm)
|
34
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm)
|
95.0
|
°C
|
ASTM D648 |
|
RTI Elec
|
80.0
|
°C
|
UL 746 |
|
RTI Imp
|
80.0
|
°C
|
UL 746 |
|
RTI Str
|
80.0
|
°C
|
UL 746 |
| Flammability |
Nominal Value
|
Unit
|
Test Method
|
|
Flame Rating
|
UL 94 | ||
|
2.50 mm
|
V-0
|
|
|
|
3.00 mm
|
V-0
|
|
|
| Optical |
Nominal Value
|
Unit
|
Test Method
|
|
Transmittance
|
89.0
|
%
|
ASTM D1003 |
| Processing Information | |||
| Injection |
Nominal Value
|
Unit
|
|
|
Drying Temperature
|
75.0 to 85.0
|
°C
|
|
|
Drying Time
|
3.0 to 5.0
|
hr
|
|
|
Suggested Max Moisture
|
0.020
|
%
|
|
|
Rear Temperature
|
220 to 240
|
°C
|
|
|
Middle Temperature
|
235 to 255
|
°C
|
|
|
Front Temperature
|
250 to 265
|
°C
|
|
|
Nozzle Temperature
|
250 to 265
|
°C
|
|
|
Processing (Melt) Temp
|
235 to 265
|
°C
|
|
|
Mold Temperature
|
50.0 to 80.0
|
°C
|
|
|
Back Pressure
|
0.981 to 3.92
|
MPa
|
|
|
Screw Speed
|
40 to 70
|
rpm
|
|
| Notes |