物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 158.6 MPa | 23000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 469 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 254 °C | 490 °F | |
| Middle Barrel Temperature | 268 °C | 515 °F | |
| Front Barrel Temperature | 285 °C | 545 °F | |
| Nozzle Temperature | 266 - 282 °C | 510 - 540 °F | |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 26.7 - 93.3 °C | 80.0 - 200 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 68.9 MPa | 10000 psi | |
| Back Pressure | 0.0689 - 0.689 MPa | 10.0 - 100 psi | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | |
尼龙中的主要品种是尼龙6和尼龙66，占绝对主导地位，其次是尼龙11，尼龙12，尼龙610，尼龙612，另外还有尼龙 1010，尼龙46，尼龙7，尼龙9，尼龙13，新品种有尼龙6I，尼龙9T和特殊尼龙MXD6（阻隔性树脂）等，尼龙的改性品种数量繁多，如增强尼龙，单体浇铸尼龙（MC尼龙），反应注射成型（RIM）尼龙，芳香族尼龙，透明尼龙，高抗冲（超韧）尼龙，电镀尼龙，导电尼龙，阻燃尼龙，尼龙与其他聚合物共混物和合金等，满足不同特殊要求，广泛用作金属，木材等传统材料代用品，作为各种结构材料。 尼龙是最重要的工程塑料，产量在五大通用工程塑料中居首位。 尼龙,是聚酰胺纤维（锦纶）是一种说法. 可制成长纤或短纤。, 工程塑料:玻璃纤维增强尼龙66(PA66+GF30)