PA66 A3HG5 25%玻璃具有吸湿性_产品资讯

BASF PA66 A3HG5 25%玻璃广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座。汽车：散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。

物性表：

Physical Properties	Metric	English	Comments

Density	1.32 g/cc	0.0477 lb/in³	ISO 1183
Water Absorption	5.7 - 6.3 %	5.7 - 6.3 %	ISO 62
Moisture Absorption at Equilibrium	1.7 - 2.1 %	1.7 - 2.1 %	(23°C/50% R.H.); ISO 62
Viscosity Test	145 cm³/g	145 cm³/g	Viscosity number; ISO 307
Linear Mold Shrinkage	0.0055 cm/cm	0.0055 in/in
Melt Flow	66 g/10 min @Load 5.00 kg, Temperature 275 °C	66 g/10 min @Load 11.0 lb, Temperature 527 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	120 MPa	17400 psi	50mm/min; ISO 527
Elongation at Yield	6.0 %	6.0 %	50mm/min; ISO 527
Modulus of Elasticity	6.50 GPa	943 ksi	ISO 527
Flexural Strength	200 MPa	29000 psi	ISO 178
Flexural Modulus	6.00 GPa	870 ksi	ISO 178
Izod Impact, Notched (ISO)	15.0 kJ/m²	7.14 ft-lb/in²	ISO 180/A
Charpy Impact Unnotched	9.00 J/cm²	42.8 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	1.80 J/cm²	8.57 ft-lb/in²	ISO 179/1eA
Tensile Creep Modulus, 1000 hours	4300 MPa	624000 psi	ISO 899

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 ohm-cm	1.00e+10 ohm-cm	IEC 60093
Surface Resistance	1.00e+10 ohm	1.00e+10 ohm	IEC 60093
Dielectric Constant	5.5 @Frequency 1.00e+6 Hz	5.5 @Frequency 1.00e+6 Hz	IEC 60250
Dissipation Factor	0.16 @Frequency 1.00e+6 Hz	0.16 @Frequency 1.00e+6 Hz	IEC 60250
	0.30 @Frequency 100 Hz	0.30 @Frequency 100 Hz	IEC 60250
Comparative Tracking Index	550 V	550 V	Test Solution A; IEC 60112

Thermal Properties	Metric	English	Comments
Specific Heat Capacity	0.340 J/g-°C	0.0813 BTU/lb-°F	DIN 52612
Thermal Conductivity	1.60 W/m-K	11.1 BTU-in/hr-ft²-°F
Melting Point	260 °C	500 °F	Din 53765
Maximum Service Temperature, Air	140 °C	284 °F	for 50% loss of tensile strength after 20,000 hr
	170 °C	338 °F	for 50% loss of tensile strength after 5,000 hr
	240 °C	464 °F

Processing Properties	Metric	English	Comments
Melt Temperature	280 - 300 °C	536 - 572 °F
Mold Temperature	80.0 - 90.0 °C	176 - 194 °F

Descriptive Properties
Color	Natural
Commercial Status	North America and Europe
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Heat stabilized or stable to heat

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。

欢迎各位客户前来咨询：

联系人：夏先生

手机：13501802636

QQ ：205730283

邮箱：205730283@qq.com

性能：PA66 聚酰胺66或尼龙66化学和物理特性PA66在聚酰胺材料中有较高的熔点。它是一种半晶体-晶体材料。PA66在较高温度也能保持较强的强度和刚度。在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是最常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。 PA66的粘性较低，因此流动性很好（但不如PA6）。这个性质可以用来加工很薄的元件。它的粘度对温度变化很敏感。PA66的收缩率在1%~2%之间，加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。 PA66对许多溶剂具有抗溶性，但对酸和其它一些氯化剂的抵抗力较弱。

PA66 A3HG5 25%玻璃 具有吸湿性

PA66 A3HG5 25%玻璃具有吸湿性