Availability
|
|
|
Additive
|
|
|
Features
|
|
|
Forms
|
|
| Physical |
Nominal Value
|
Unit
|
Test Method
|
|
Specific Gravity
|
1.16
|
g/cm³
|
ASTM D792 |
|
Molding Shrinkage - Flow
|
1.1 to 1.4
|
%
|
ASTM D955 |
|
Water Absorption (24 hr)
|
1.1
|
%
|
ASTM D570 |
| Hardness |
Nominal Value
|
Unit
|
Test Method
|
|
Rockwell Hardness
|
ASTM D785 | ||
|
M-Scale
|
85
|
|
|
|
R-Scale
|
121
|
|
| Mechanical |
Nominal Value
|
Unit
|
Test Method
|
|
Tensile Strength (Yield)
|
89.6
|
MPa
|
ASTM D638 |
|
Tensile Elongation (Break)
|
8.0
|
%
|
ASTM D638 |
|
Flexural Modulus
|
3170
|
MPa
|
ASTM D790 |
|
Flexural Strength (Yield)
|
117
|
MPa
|
ASTM D790 |
|
Compressive Strength
|
103
|
MPa
|
ASTM D695 |
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Notched Izod Impact (23°C, 3.18 mm)
|
37
|
J/m
|
ASTM D256 |
| Thermal |
Nominal Value
|
Unit
|
Test Method
|
|
Deflection Temperature Under Load
|
ASTM D648 | ||
|
0.45 MPa, Unannealed
|
196
|
°C
|
|
|
1.8 MPa, Unannealed
|
78.9
|
°C
|
|
|
Melting Temperature
|
254 to 266
|
°C
|
|
|
CLTE - Flow
|
0.000072
|
cm/cm/°C
|
ASTM D696 |
|
Thermal Conductivity
|
0.25
|
W/m/K
|
ASTM C177 |
| Electrical |
Nominal Value
|
Unit
|
Test Method
|
|
Volume Resistivity
|
2.0E+14
|
ohm·cm
|
ASTM D257 |
|
Dielectric Strength
|
18
|
kV/mm
|
ASTM D149 |