PA66 TA250G33 33%玻璃纤维增强聚酰胺化学式：[-NH（CH2）6－NHCO(CH2)4CO]n－性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

Physical Properties	Metric	English	Comments
物性表：
Density	1.38 g/cc	0.0499 lb/in³	ASTM D792
Water Absorption	0.70 %	0.70 %	23°C/24 hr; ASTM D570
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	190 MPa	27600 psi	ASTM D638
Elongation at Break	3.0 %	3.0 %	ASTM D638
Flexural Yield Strength	280 MPa	40600 psi	ASTM D790
Flexural Modulus	9.00 GPa	1310 ksi	ASTM D790
Izod Impact, Notched	1.30 J/cm	2.44 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	260 °C	500 °F	ASTM D2133
Deflection Temperature at 0.46 MPa (66 psi)	260 °C	500 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	252 °C	486 °F	ASTM D648
Flammability, UL94	HB	HB

Processing Properties	Metric	English	Comments
Processing Temperature	280 - 300 °C	536 - 572 °F
Mold Temperature	80.0 - 100 °C	176 - 212 °F

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。

欢迎各位客户前来咨询：

联系人：夏先生

手机：13501802636

QQ ：205730283

邮箱：205730283@qq.com

图：

塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。