| 物性表： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Water Absorption | 1.2 % @Time 86400 sec |
1.2 % @Time 24.0 hour |
|
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 73.5 MPa | 10700 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 2.65 GPa | 384 ksi | ASTM D790 |
| Izod Impact, Notched | 0.686 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 228 °C | 442 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
PA66 ta210ir冲击改性类：聚合物；热塑性；尼龙；尼龙66；尼龙66，品位的影响
材料说明：聚酰胺（尼龙）树脂：tekamid是e-polymers工程聚合物聚酰胺- 66，6的注册商标，和66 / 6，提供全方位的聚酰胺（尼龙）注塑成型和挤出树脂。tekamid广泛被应用于以其卓越的机械工业汽车零部件制造，热性能和化学性能。
L系列：一般注射润滑剂
T系列：冲击改性，超硬制品
G系列：玻璃钢制品
F系列：阻燃产品达到V-0级
M系列：矿物或混合产品
JN系列：PA66、PA6／PPE，PPE合金（无筋，GF增强，MF钢筋）
H系列：PA6／ABS，ABS合金（增强PA66，GF增强，MR增强）
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。