 PA66 RF006XXP 塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。

Physical Properties	Metric	English	Comments
Density	1.37 g/cc	0.0495 lb/in³	ISO 1183
Moisture Absorption	1.30 % @Temperature 23.0 °C	1.30 % @Temperature 73.4 °F	50% RH; ISO 62
Water Absorption at Saturation	4.5 % @Temperature 23.0 °C	4.5 % @Temperature 73.4 °F	ISO 62
Linear Mold Shrinkage, Flow	0.0020 - 0.0040 cm/cm	0.0020 - 0.0040 in/in	on Tensile Bar; E2P method
Mechanical Properties	Metric	English	Comments
Hardness, Rockwell L	113	113	ISO 2039-2
Tensile Strength at Break	175 MPa	25400 psi	5 mm/min; ISO 527
Elongation at Break	3.0 %	3.0 %	5 mm/min; ISO 527
Tensile Modulus	9.50 GPa	1380 ksi	1 mm/min; ISO 527
Flexural Strength	265 MPa	38400 psi	break, 2 mm/min; ISO 178
Flexural Modulus	9.00 GPa	1310 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	8.00 kJ/m² @Temperature -30.0 °C	3.81 ft-lb/in² @Temperature -22.0 °F	80x10x4; ISO 179/1eA
	8.00 kJ/m² @Temperature -40.0 °C	3.81 ft-lb/in² @Temperature -40.0 °F	80x10x4; ISO 179/1eA
	9.00 kJ/m² @Temperature -20.0 °C	4.28 ft-lb/in² @Temperature -4.00 °F	80x10x4; ISO 179/1eA
	10.0 kJ/m² @Temperature 23.0 °C	4.76 ft-lb/in² @Temperature 73.4 °F	80x10x4; ISO 179/1eA
Charpy Impact Unnotched	5.50 J/cm² @Temperature -30.0 °C	26.2 ft-lb/in² @Temperature -22.0 °F	Edgew 80x10x4 sp=62; ISO 179/1eU
	7.50 J/cm² @Temperature 23.0 °C	35.7 ft-lb/in² @Temperature 73.4 °F	Edgew 80x10x4 sp=62; ISO 179/1eU
Charpy Impact, Notched	0.700 J/cm² @Temperature -30.0 °C	3.33 ft-lb/in² @Temperature -22.0 °F	Edgew 80x10x4 sp=62; ISO 179/1eA
	0.800 J/cm² @Temperature 23.0 °C	3.81 ft-lb/in² @Temperature 73.4 °F	Edgew 80x10x4 sp=62; ISO 179/1eA
Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+16 ohm-cm	>= 1.00e+16 ohm-cm	IEC 60093
Surface Resistance	>= 1.00e+16 ohm	>= 1.00e+16 ohm	IEC 60093
Dielectric Constant	3.2 @Frequency 1.00e+6 Hz	3.2 @Frequency 1.00e+6 Hz	IEC 60250
	3.4 @Frequency 50.0 - 60.0 Hz	3.4 @Frequency 50.0 - 60.0 Hz	IEC 60250
Dielectric Strength	19.0 kV/mm @Thickness 3.20 mm	483 kV/in @Thickness 0.126 in	in oil; IEC 60243-1
Dissipation Factor	0.0068 @Frequency 50.0 - 60.0 Hz	0.0068 @Frequency 50.0 - 60.0 Hz	IEC 60250
	0.015 @Frequency 1.00e+6 Hz	0.015 @Frequency 1.00e+6 Hz	IEC 60250
Comparative Tracking Index	400 V	400 V	M; IEC 60112
	500 V	500 V	IEC 60112
Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	25.0 µm/m-°C @Temperature 23.0 - 60.0 °C	13.9 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
CTE, linear, Transverse to Flow	75.0 µm/m-°C @Temperature 23.0 - 60.0 °C	41.7 µin/in-°F @Temperature 73.4 - 140 °F	ISO 11359-2
Thermal Conductivity	0.330 W/m-K	2.29 BTU-in/hr-ft²-°F	ASTM E1530
Hot Ball Pressure Test	123 - 127 °C	253 - 261 °F	IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi)	260 °C	500 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi)	248 °C	478 °F	Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point	255 °C	491 °F	B/120; ISO 306
	258 °C	496 °F	B/50; ISO 306
UL RTI, Electrical	65.0 °C	149 °F
UL RTI, Mechanical with Impact	65.0 °C	149 °F
UL RTI, Mechanical without Impact	65.0 °C	149 °F
Flammability, UL94	HB @Thickness 0.750 mm	HB @Thickness 0.0295 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in
Flame Spread	2.00 mm/min @Thickness 3.00 mm	0.0787 in/min @Thickness 0.118 in	FMVSS Burning Speed
	6.00 mm/min @Thickness 2.00 mm	0.236 in/min @Thickness 0.0787 in	FMVSS Burning Speed
Glow Wire Test	650 °C @Thickness 2.00 mm	1200 °F @Thickness 0.0787 in	IEC 60695-2-12
Processing Properties	Metric	English	Comments
Zone 1	260 - 280 °C	500 - 536 °F
Zone 2	270 - 280 °C	518 - 536 °F
Zone 3	270 - 290 °C	518 - 554 °F
Melt Temperature	270 - 290 °C	518 - 554 °F
Mold Temperature	60.0 - 90.0 °C	140 - 194 °F
Drying Temperature	75.0 - 85.0 °C @Time 14400 - 21600 sec	167 - 185 °F @Time 4.00 - 6.00 hour
Moisture Content	0.20 %	0.20 %