颗粒： 
物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 114 MPa | 16500 psi | ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | ISO 527 |
| Flexural Strength | 161 MPa | 23400 psi | ISO 178 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Processing Properties | Metric | English | Comments |
| Zone 1 | 260 - 280 °C | 500 - 536 °F | |
| Zone 2 | 270 - 285 °C | 518 - 545 °F | |
| Zone 3 | 265 - 280 °C | 509 - 536 °F | |
| Melt Temperature | 265 - 280 °C | 509 - 536 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % | |
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。