颗粒图：
物性表：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 | ||
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 119 MPa | 17300 psi | ASTM D638 | ||
| 120 MPa | 17400 psi | 5mm/min; ISO 527-2/1A | |||
| Elongation at Break | 1.86 % | 1.86 % | 5mm/min; ISO 527-2/1A | ||
| 1.6 % @Temperature 22.8 °C |
1.6 % @Temperature 73.0 °F |
ASTM D638 | |||
| Tensile Modulus | 9.20 GPa | 1330 ksi | 1mm/min; ISO 527-2/1A | ||
| 9.03 GPa @Temperature 22.8 °C |
1310 ksi @Temperature 73.0 °F |
ASTM D638 | |||
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 | ||
| 183 MPa | 26600 psi | ASTM D790 | |||
| Flexural Modulus | 7.80 GPa | 1130 ksi | ISO 178 | ||
| 8.20 GPa @Temperature 22.8 °C |
1190 ksi @Temperature 73.0 °F |
ASTM D790 | |||
| Izod Impact, Notched | 1.44 J/cm | 2.70 ft-lb/in | ASTM D256 | ||
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 246 °C | 475 °F | ISO 75-1, -2 | ||
| 246 °C | 475 °F | ASTM D648 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| 80.0 - 100 °C | 176 - 212 °F | Cavity temperature | |||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 285 - 295 °C | 545 - 563 °F | |||
| Zone 2 | 290 - 300 °C | 554 - 572 °F | |||
| Zone 3 | 300 - 310 °C | 572 - 590 °F | |||
| Zone 4 | 300 - 315 °C | 572 - 599 °F | |||
| Die Temperature | 300 - 315 °C | 572 - 599 °F | |||
| Melt Temperature | 300 - 315 °C | 572 - 599 °F | |||
| Mold Temperature | 85.0 - 95.0 °C | 185 - 203 °F | |||
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | 0.18 % | 0.18 % | Necessary low maximum residual | ||
| Dew Point | <= -30.0 °C | <= -22.0 °F | Pre-drying | ||
| De |
|||||
| Injection molding | Yes | ||||
| Longer pre-drying times/storage | Material can be over dried and may discolor. | ||||
用途：广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座。
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。