| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 | ||
| Viscosity Test | 140 cm³/g | 140 cm³/g | ISO 307, 1157, 1628 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 180 MPa | 26100 psi | 5mm/min; ISO 527-2/1A | ||
| Tensile Strength | 130 MPa @Temperature 80.0 °C |
18900 psi @Temperature 176 °F |
ISO 527-1, -2 | ||
| Elongation at Break | 1.5 % | 1.5 % | 5mm/min; ISO 527-2/1A | ||
| 2.0 % @Temperature 80.0 °C |
2.0 % @Temperature 176 °F |
ISO 527-1, -2 | |||
| Tensile Modulus | 13.7 GPa | 1990 ksi | 1mm/min; ISO 527-2/1A | ||
| 9.00 GPa @Temperature 80.0 °C |
1310 ksi @Temperature 176 °F |
ISO 527-1, -2 | |||
| Flexural Strength | 260 MPa | 37700 psi | ISO 178 | ||
| 250 MPa @Temperature 80.0 °C |
36300 psi @Temperature 176 °F |
ISO 178 | |||
| Flexural Modulus | 12.6 GPa | 1830 ksi | ISO 178 | ||
| 8.00 GPa @Temperature 80.0 °C |
1160 ksi @Temperature 176 °F |
ISO 178 | |||
| Izod Impact, Notched (ISO) | 24.0 kJ/m² | 11.4 ft-lb/in² | ISO 180/1A | ||
| 35.0 kJ/m² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A | |||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU | ||
| 4.10 J/cm² @Temperature -30.0 °C |
19.5 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 2.30 J/cm² | 10.9 ft-lb/in² | ISO 179/1eA | ||
| 2.30 J/cm² @Temperature -30.0 °C |
10.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 261 °C | 502 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 240 °C | 464 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| 90.0 - 120 °C | 194 - 248 °F | Cavity temperature | |||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 265 - 275 °C | 509 - 527 °F | |||
| Zone 2 | 275 - 285 °C | 527 - 545 °F | |||
| Zone 3 | 285 - 295 °C | 545 - 563 °F | |||
| Zone 4 | 295 - 305 °C | 563 - 581 °F | |||
| Die Temperature | 305 - 315 °C | 581 - 599 °F | |||
| Melt Temperature | 300 - 315 °C | 572 - 599 °F | in the screw anteroom | ||
| 305 - 315 °C | 581 - 599 °F | ||||
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |||
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | 0.15 % | 0.15 % | Necessary low maximum residual | ||
| Dew Point | <= -30.0 °C | <= -22.0 °F | Pre-drying | ||
| Injection Pressure | 120 - 150 MPa | 17400 - 21800 psi | |||
| Hold Pressure | 50.0 - 80.0 MPa | 7250 - 11600 psi | |||
| Back Pressure | 3.00 MPa | 435 psi | |||
| Screw Speed | 25 rpm @Diameter 75.0 mm |
25 rpm @Diameter 2.95 in |
|||
| 35 rpm @Diameter 55.0 mm |
35 rpm @Diameter 2.17 in |
||||
| 50 rpm @Diameter 40.0 mm |
50 rpm @Diameter 1.57 in |
||||
| Hot-Working Temperature | 300 - 315 °C | 572 - 599 °F | |||
| De |
|||||
| Heat stabilized/stable to heat | Yes | ||||
| Injection molding | Yes | ||||
| Injection speed | medium | ||||
| Sheet extrusion | Yes | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。