| 物性表： | |||||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 260 MPa | 37700 psi | 5mm/min; ISO 527-2/1A | ||
| Tensile Strength | 150 MPa @Temperature 80.0 °C |
21800 psi @Temperature 176 °F |
ISO 527-1, -2 | ||
| Elongation at Break | 2.2 % | 2.2 % | 5mm/min; ISO 527-2/1A | ||
| 2.8 % @Temperature 80.0 °C |
2.8 % @Temperature 176 °F |
ISO 527-1, -2 | |||
| Tensile Modulus | 16.6 GPa | 2410 ksi | 1mm/min; ISO 527-2/1A | ||
| 8.05 GPa @Temperature 80.0 °C |
1170 ksi @Temperature 176 °F |
ISO 527-1, -2 | |||
| Flexural Strength | 380 MPa | 55100 psi | ISO 178 | ||
| 260 MPa @Temperature 80.0 °C |
37700 psi @Temperature 176 °F |
ISO 178 | |||
| Flexural Modulus | 13.5 GPa | 1960 ksi | ISO 178 | ||
| 9.50 GPa @Temperature 80.0 °C |
1380 ksi @Temperature 176 °F |
ISO 178 | |||
| Charpy Impact Unnotched | 10.0 J/cm² | 47.6 ft-lb/in² | ISO 179/1eU | ||
| 8.00 J/cm² @Temperature -30.0 °C |
38.1 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eA | ||
| 4.20 J/cm² @Temperature -30.0 °C |
20.0 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 240 °C | 464 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 220 °C | 428 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| 90.0 - 120 °C | 194 - 248 °F | Cavity temperature | |||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 280 - 285 °C | 536 - 545 °F | |||
| Zone 2 | 280 - 290 °C | 536 - 554 °F | |||
| Zone 3 | 290 - 300 °C | 554 - 572 °F | |||
| Zone 4 | 300 - 310 °C | 572 - 590 °F | |||
| Die Temperature | 310 - 320 °C | 590 - 608 °F | |||
| Melt Temperature | 310 - 320 °C | 590 - 608 °F | |||
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | 0.15 % | 0.15 % | Necessary low maximum residual | ||
| Injection Pressure | 120 - 150 MPa | 17400 - 21800 psi | |||
| Hold Pressure | 50.0 - 80.0 MPa | 7250 - 11600 psi | |||
| Back Pressure | 3.00 MPa | 435 psi | |||
| Screw Speed | 25 rpm @Diameter 75.0 mm |
25 rpm @Diameter 2.95 in |
|||
| 35 rpm @Diameter 55.0 mm |
35 rpm @Diameter 2.17 in |
||||
| 50 rpm @Diameter 40.0 mm |
50 rpm @Diameter 1.57 in |
||||
| Hot-Working Temperature | 300 - 315 °C | 572 - 599 °F | |||
| De |
|||||
| Injection speed | medium | ||||
用途：广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座。
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com