PA66-GF60-02-US 耐韧、_产品资讯

PA66-GF60-02-US 塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物，具有可塑性。密度（g/cm3） 1．10-1．14；拉伸强度(MPa) 60. 0-80．0；洛氏硬度118；熔点252℃；脆化温度-30℃；热分解温度大于350℃；连续耐热80-120℃；冲击强度（kJ/m2） 60-100；静弯曲强度(MPa) 1 00-120；马丁耐热(℃) 50-60；弯曲弹性模量 (MPa) 2000～3000；体积电阻率（Ωcm） 1.83×1015；平衡吸水率2．5%；介电常数 1．63。

颗粒样图：

物性表：

Physical Properties	Metric	English	Comments

Specific Gravity	1.69 g/cc	1.69 g/cc	ASTM D792
Density	1.69 g/cc	0.0611 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.00050 - 0.0010 cm/cm	0.00050 - 0.0010 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.0010 - 0.0020 cm/cm	0.0010 - 0.0020 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	280 MPa	40600 psi	5mm/min; ISO 527-2/1A
	318 MPa	46100 psi	ASTM D638
	173 MPa @Temperature 121 °C	25100 psi @Temperature 250 °F	ASTM D638
	354 MPa @Temperature -40.0 °C	51300 psi @Temperature -40.0 °F	ASTM D638
Elongation at Break	1.7 %	1.7 %	5mm/min; ISO 527-2/1A
	1.8 % @Temperature 22.8 °C	1.8 % @Temperature 73.0 °F	ASTM D638
	1.9 % @Temperature -40.0 °C	1.9 % @Temperature -40.0 °F	ASTM D638
	2.0 % @Temperature 80.0 °C	2.0 % @Temperature 176 °F	ISO 527-1, -2
	2.2 % @Temperature 121 °C	2.2 % @Temperature 250 °F	ASTM D638
Tensile Modulus	21.6 GPa	3130 ksi	1mm/min; ISO 527-2/1A
	11.9 GPa @Temperature 80.0 °C	1730 ksi @Temperature 176 °F	ISO 527-1, -2
	13.3 GPa @Temperature 121 °C	1930 ksi @Temperature 250 °F	ASTM D638
	20.86 GPa @Temperature -40.0 °C	3025 ksi @Temperature -40.0 °F	ASTM D638
	23.2 GPa @Temperature 22.8 °C	3360 ksi @Temperature 73.0 °F	ASTM D638
Flexural Strength	460 MPa	66700 psi	ISO 178
	461 MPa	66900 psi	ASTM D790
	228 MPa @Temperature 121 °C	33000 psi @Temperature 250 °F	ASTM D790
	545 MPa @Temperature -40.0 °C	79000 psi @Temperature -40.0 °F	ASTM D790
Flexural Modulus	19.4 GPa	2810 ksi	ISO 178
	10.3 GPa @Temperature 121 °C	1490 ksi @Temperature 250 °F	ASTM D790
	18.7 GPa @Temperature 22.8 °C	2710 ksi @Temperature 73.0 °F	ASTM D790
	19.3 GPa @Temperature -40.0 °C	2800 ksi @Temperature -40.0 °F	ASTM D790
Izod Impact, Notched	6.62 J/cm	12.4 ft-lb/in	ASTM D256
	7.63 J/cm @Temperature 149 °C	14.3 ft-lb/in @Temperature 300 °F	ASTM D256
	7.69 J/cm @Temperature -40.0 °C	14.4 ft-lb/in @Temperature -40.0 °F	ASTM D256
Charpy Impact, Notched	5.40 J/cm²	25.7 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	263 °C	505 °F	ASTM D648
	263 °C	505 °F	ISO 75-1, -2

Processing Properties	Metric	English	Comments
Processing Temperature	70.0 - 80.0 °C	158 - 176 °F
	80.0 - 100 °C	176 - 212 °F	Cavity temperature
Feed Temperature	20.0 - 50.0 °C	68.0 - 122 °F
Zone 1	285 - 295 °C	545 - 563 °F
Zone 2	290 - 300 °C	554 - 572 °F
Zone 3	300 - 310 °C	572 - 590 °F
Zone 4	300 - 315 °C	572 - 599 °F
Die Temperature	300 - 315 °C	572 - 599 °F
Melt Temperature	300 - 315 °C	572 - 599 °F
Mold Temperature	90.0 - 100 °C	194 - 212 °F
Drying Temperature	70.0 - 80.0 °C	158 - 176 °F
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour
Moisture Content	0.18 %	0.18 %	Necessary low maximum residual
Dew Point	<= -30.0 °C	<= -22.0 °F	Pre-drying

Descriptive Properties
Injection molding	Yes
Longer pre-drying times/storage	Material can be over dried and may discolor.

应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。