| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.24 g/cc @Temperature 23.0 °C |
1.24 g/cc @Temperature 73.4 °F |
ASTM D792 | ||
| Water Absorption | 0.60 % @Temperature 23.0 °C, Time 86400 sec |
0.60 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 | ||
| Linear Mold Shrinkage | 0.0050 - 0.012 cm/cm @Temperature 23.0 °C |
0.0050 - 0.012 in/in @Temperature 73.4 °F |
ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM D785 | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | 10mm/min; ASTM D638 | ||
| Flexural Strength | 180 MPa | 26100 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 6.10 GPa | 885 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | 0.850 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.59 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 253 °C @Thickness 6.40 mm |
487 °F @Thickness 0.252 in |
ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C @Thickness 6.40 mm |
469 °F @Thickness 0.252 in |
ASTM D648 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|||
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 310 °C | <= 590 °F | |||
| Rear Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Start Point: 265°C | ||
| Middle Barrel Temperature | 265 - 300 °C | 509 - 572 °F | Start Point: 285°C | ||
| Front Barrel Temperature | 275 - 305 °C | 527 - 581 °F | Start Point: 285°C | ||
| Melt Temperature | 275 - 310 °C | 527 - 590 °F | Start Point: 285°C | ||
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Start Point: 60°C | ||
| Drying Temperature | 90.0 - 110 °C @Time 14400 - 21600 sec |
194 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry | ||
| De |
|||||
| Glass Fiber Content (%) | 15 | ||||
| Injection Speed | Moderate to High | ||||
用途：广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座。
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com