颗粒样图：
应用：广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO 1183-A |
| Water Absorption | 0.75 % | 0.75 % | 24 hours in water at 23°C; ISO 62. |
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 210 MPa | 30500 psi | ISO 527 |
| Tensile Strength, Yield | 210 MPa | 30500 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 11.4 GPa | 1650 ksi | ISO 527 |
| Flexural Yield Strength | 286 MPa | 41500 psi | ISO 178 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 |
| Izod Impact Resistance | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 9.50 J/cm² | 45.2 ft-lb/in² | ISO 179/1EA-1993 |
| Charpy Impact, Notched | 1.35 J/cm² | 6.42 ft-lb/in² | ISO 179/1EA-1993 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Surface Resistance | 6.00e+14 ohm | 6.00e+14 ohm | IEC 93 |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz |
3.7 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 243-1 |
| Dissipation Factor | 0.010 @Frequency 1e+6 Hz |
0.010 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 22.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
12.2 µin/in-°F @Temperature 73.4 - 185 °F |
ASTM E831 |
| Melting Point | 263 °C | 505 °F | ISO 3146-C |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO 1210/UL 94 |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |