PA66 A 217 PA66, 注塑成型、_产品资讯

PA66 A 217 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

物性表:

Physical Properties	Metric	English	Comments

Density	1.14 g/cc	0.0412 lb/in³	ISO 1183/A
Water Absorption	1.3 % @Temperature 23.0 °C, Time 86400 sec	1.3 % @Temperature 73.4 °F, Time 24.0 hour	ISO 62
	1.5 % @Temperature 100 °C, Time 1800 sec	1.5 % @Temperature 212 °F, Time 0.500 hour	ISO 62
Linear Mold Shrinkage	0.010 cm/cm	0.010 in/in	Isotropy
Linear Mold Shrinkage, Flow	0.019 cm/cm	0.019 in/in
Linear Mold Shrinkage, Transverse	0.019 cm/cm	0.019 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	65.0 MPa	9430 psi	ISO 527 Type 1A
Tensile Stress	59.0 MPa @Strain 2.00 %	8560 psi @Strain 2.00 %
	81.0 MPa @Strain 4.00 %	11700 psi @Strain 4.00 %
	83.0 MPa @Strain 6.00 %	12000 psi @Strain 6.00 %
Tensile Strength, Yield	85.0 MPa	12300 psi	ASTM D638
	88.0 MPa	12800 psi	ISO 527 type 1 A
Elongation at Break	20 %	20 %	ISO 527 Type 1A
	30 %	30 %	ASTM D638
Tensile Modulus	3.30 GPa	479 ksi	ISO 527 Type 1A
Flexural Strength	125 MPa	18100 psi	ASTM D790
	130 MPa	18900 psi	ISO 178
Flexural Modulus	3.10 GPa	450 ksi	ISO 178
	3.50 GPa	508 ksi	ASTM D790
Izod Impact, Notched (ISO)	4.00 kJ/m²	1.90 ft-lb/in²	ISO 180/1A
	80.0 kJ/m²	38.1 ft-lb/in²	ASTM D256
Izod Impact, Unnotched (ISO)	NB	NB	ISO 180/1U
Charpy Impact Unnotched	NB	NB	ISO 179/1eU
Charpy Impact, Notched	0.430 J/cm²	2.05 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	263 °C	505 °F	ISO 11357
Deflection Temperature at 0.46 MPa (66 psi)	220 °C	428 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	75.0 °C	167 °F	ISO 75/Af
Flammability, UL94	V-2 @Thickness 1.60 mm	V-2 @Thickness 0.0630 in	1210
	V-2 @Thickness 3.20 mm	V-2 @Thickness 0.126 in	1210
Oxygen Index	26 %	26 %	ISO 4589
Glow Wire Test	650 °C @Thickness 0.800 mm	1200 °F @Thickness 0.0315 in	ISO 60695-2-12
	650 °C @Thickness 1.60 mm	1200 °F @Thickness 0.0630 in	ISO 60695-2-12
	650 °C @Thickness 1.60 mm	1200 °F @Thickness 0.0630 in	Ignition Temperature; ISO 60695-2-13

Processing Properties	Metric	English	Comments
Feed Temperature	265 - 275 °C	509 - 527 °F
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F
Drying Temperature	80.0 °C	176 °F
Moisture Content	<= 0.20 %	<= 0.20 %

Descriptive Properties
Compression Zone	270-280°C
Mixing Zone	280-290°C

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。