PA66 A 218HP V50 35%玻璃纤维、

PA66 A 218HP V50 是一种半晶体-晶体材料。PA66在较高温度也能保持较强的强度和刚度。PA66 A 218HP V50 在产品设计时,一定要考虑吸湿性对几何稳定性的影响。PA66 A 218HP V50 为了提高PA66的机械特性,经常加入各种各样的改性剂。玻璃就是最常见的添加剂,有时为了提高抗冲击性还加入合成橡胶,如EPDM和SBR等。 PA66的粘性较低,因此流动性很好(但不如PA6)。
PA66 A 218HP V50 塑胶原料为半透明或不透明乳白包或带黄色颗粒状结晶形聚合物,具有可塑性。密度(g/cm3) 1.10-1.14;拉伸强度(MPa) 60. 0-80.0;洛氏硬度118;熔点252℃;脆化温度-30℃;热分解温度大于350℃;连续耐热80-120℃;冲击强度(kJ/m2) 60-100;静弯曲强度(MPa) 1 00-120;马丁耐热(℃) 50-60;弯曲弹性模量 (MPa) 2000~3000;体积电阻率(Ωcm) 1.83×1015;平衡吸水率2.5%;介电常数 1.63。
颗粒样图:B颗粒09   
 
物性表:
 
Physical Properties Metric English Comments
Density  1.52 g/cc 0.0549 lb/in³ ISO 1183/A
Linear Mold Shrinkage  0.0060 cm/cm 0.0060 in/in Isotropy
Linear Mold Shrinkage, Flow  0.0030 cm/cm 0.0030 in/in  
Linear Mold Shrinkage, Transverse  0.0050 cm/cm 0.0050 in/in  
  0.0090 cm/cm 0.0090 in/in ISO 294-4
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  200 MPa 29000 psi ISO 527 Type 1A
Tensile Stress    39.0 MPa
@Strain 1.00 %,
Temperature 200 °C
5660 psi
@Strain 1.00 %,
Temperature 392 °F
 
  45.0 MPa
@Strain 2.00 %,
Temperature 200 °C
6530 psi
@Strain 2.00 %,
Temperature 392 °F
 
  48.0 MPa
@Strain 3.00 %,
Temperature 200 °C
6960 psi
@Strain 3.00 %,
Temperature 392 °F
 
  50.0 MPa
@Strain 4.00 %,
Temperature 200 °C
7250 psi
@Strain 4.00 %,
Temperature 392 °F
 
  80.0 MPa
@Strain 0.500 %,
Temperature 23.0 °C
11600 psi
@Strain 0.500 %,
Temperature 73.4 °F
 
  150 MPa
@Strain 1.00 %,
Temperature 23.0 °C
21800 psi
@Strain 1.00 %,
Temperature 73.4 °F
 
  180 MPa
@Strain 1.50 %,
Temperature 23.0 °C
26100 psi
@Strain 1.50 %,
Temperature 73.4 °F
 
Elongation at Break  2.0 % 2.0 % ISO 527 Type 1A
Tensile Modulus  15.0 GPa 2180 ksi ISO 527 Type 1A
Flexural Strength  280 MPa 40600 psi ASTM D790
  320 MPa 46400 psi ISO 178
Flexural Modulus  13.5 GPa 1960 ksi ISO 178
  13.5 GPa 1960 ksi ASTM D790
Izod Impact, Notched (ISO)  20.0 kJ/m² 9.52 ft-lb/in² ISO 180/1eA
Izod Impact, Unnotched (ISO)  80.0 kJ/m² 38.1 ft-lb/in² ISO 180/1eU
Charpy Impact Unnotched  8.50 J/cm² 40.4 ft-lb/in² ISO 179/1eU
Charpy Impact, Notched  1.70 J/cm² 8.09 ft-lb/in² ISO 179/1eA
 
Thermal Properties Metric English Comments
Melting Point  263 °C 505 °F ISO 11357
Deflection Temperature at 0.46 MPa (66 psi)  260 °C 500 °F ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)  253 °C 487 °F ISO 75/Af
Flammability, UL94    HB
@Thickness 0.800 mm
HB
@Thickness 0.0315 in
1210
  HB
@Thickness 1.60 mm
HB
@Thickness 0.0630 in
1210
  HB
@Thickness 3.20 mm
HB
@Thickness 0.126 in
1210
 
Processing Properties Metric English Comments
Feed Temperature  265 - 275 °C 509 - 527 °F  
Mold Temperature  80.0 - 110 °C 176 - 230 °F  
Drying Temperature  80.0 °C 176 °F  
Moisture Content  <= 0.12 % <= 0.12 %  
 
Descriptive Properties
Compression Zone 270-280°C  
Mixing Zone 280-290°C
应用:广泛用于制造机械、汽车、化学与电气装置的零件,如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包内层等。
 
上海松翰塑化科技有限公司,供应原料,品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询:
联系人: 夏先生  
手  机:13501802636   
QQ    :205730283  
邮 箱 :205730283@qq.com 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-26413.html

免责声明: 本文 PA66 A 218HP V50 35%玻璃纤维、 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4