物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Water Absorption | 3.3 % | 3.3 % | |
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | Humidity Absorption |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
8.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 3.4 % | 3.4 % | 50 mm/min |
| Tensile Modulus | 2.30 GPa | 334 ksi | 1 mm/min |
| Tensile Creep Modulus, 1 hour | 2030 MPa | 294000 psi | |
| Tensile Creep Modulus, 1000 hours | 870 MPa | 126000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| 3.1 @Frequency 1e+6 Hz |
3.1 @Frequency 1e+6 Hz |
||
| Dielectric Strength | 38.0 kV/mm | 965 kV/in | |
| Dissipation Factor | 0.025 @Frequency 1e+6 Hz |
0.025 @Frequency 1e+6 Hz |
|
| 0.062 @Frequency 100 Hz |
0.062 @Frequency 100 Hz |
||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 93.0 µm/m-°C @Temperature 20.0 °C |
51.7 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 133 µm/m-°C @Temperature 20.0 °C |
73.9 µin/in-°F @Temperature 68.0 °F |
|
| Melting Point | 220 °C | 428 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | |
| Vicat Softening Point | 129 °C | 264 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。