PA6 8231G HS 14%玻璃、

PA6 8231G HS 的收缩率在1%~2%之间。PA6 8231G HS 加入玻璃纤维添加剂可以将收缩率降低到0.2%~1% 。PA6 8231G HS 收缩率在流程方向和与流程方向相垂直方向上的相异是较大的。PA66对许多溶剂具有抗溶性,但对酸和其它一些氯化剂的抵抗力较弱。
PA6 8231G HS 性状为半透明或不透明乳白色结晶形聚合物,具有可塑性。密度1.15g/cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。 连续耐热80-120℃,平衡吸水率2.5%。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀,但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性,机械强度较高。但吸水性较大,因而尺寸稳定性较差。
颗粒:images (9)  、
 
物性表:
 
Physical Properties Metric English Comments
Density  1.067 g/cc 0.03855 lb/in³ Melt; ISO 1183
  1.23 g/cc 0.0444 lb/in³ ISO 1183
Water Absorption  1.4 % 1.4 % 24 hour; ISO Test
  8.1 % 8.1 % ISO 62
Moisture Absorption at Equilibrium  2.3 % 2.3 % 23°C/50% R.H.; ISO 62
Viscosity Measurement  50 50 Formic Acid
Linear Mold Shrinkage  0.0050 cm/cm 0.0050 in/in ASTM Data; MD
 
Mechanical Properties Metric English Comments
Hardness, Rockwell R  121 121 ASTM Test
Tensile Strength at Break  140 MPa 20300 psi 0.2 in/min; ASTM Test
   50.0 MPa
@Temperature 120 °C
7250 psi
@Temperature 248 °F
ISO Data
  50.0 MPa
@Temperature 120 °C
7250 psi
@Temperature 248 °F
ASTM Test
  60.0 MPa
@Temperature 80.0 °C
8700 psi
@Temperature 176 °F
ASTM Test
  60.0 MPa
@Temperature 80.0 °C
8700 psi
@Temperature 176 °F
ISO Data
  160 MPa
@Temperature -40.0 °C
23200 psi
@Temperature -40.0 °F
ASTM Test
  160 MPa
@Temperature -40.0 °C
23200 psi
@Temperature -40.0 °F
ISO Data
Tensile Strength, Ultimate  140 MPa 20300 psi 5mm/min; ISO 527
Elongation at Break  4.0 % 4.0 % 5mm/min; ISO 527
  4.0 % 4.0 % 0.2 in/min; ASTM Test
   3.0 %
@Temperature -40.0 °C
3.0 %
@Temperature -40.0 °F
ASTM Test
  3.0 %
@Temperature -40.0 °C
3.0 %
@Temperature -40.0 °F
ISO Data
  7.0 %
@Temperature 120 °C
7.0 %
@Temperature 248 °F
ISO Data
  7.0 %
@Temperature 120 °C
7.0 %
@Temperature 248 °F
ASTM Test
  8.0 %
@Temperature 80.0 °C
8.0 %
@Temperature 176 °F
ASTM Test
  8.0 %
@Temperature 80.0 °C
8.0 %
@Temperature 176 °F
ISO Data
Tensile Modulus  5.96 GPa 864 ksi 1mm/min; ISO 527
   2.09 GPa
@Temperature 120 °C
303 ksi
@Temperature 248 °F
ISO Data
  2.47 GPa
@Temperature 80.0 °C
358 ksi
@Temperature 176 °F
ISO Data
  5.95 GPa
@Temperature -40.0 °C
863 ksi
@Temperature -40.0 °F
ISO Data
Flexural Strength  160 MPa 23200 psi ISO Data
  172 MPa 24900 psi ASTM Test
   76.0 MPa
@Temperature 120 °C
11000 psi
@Temperature 248 °F
ASTM Test
  90.0 MPa
@Temperature 93.0 °C
13100 psi
@Temperature 199 °F
ASTM Test
  110 MPa
@Temperature 65.0 °C
16000 psi
@Temperature 149 °F
ASTM Test
  214 MPa
@Temperature -40.0 °C
31000 psi
@Temperature -40.0 °F
ASTM Test
Flexural Modulus  4.77 GPa 692 ksi ISO Data
  5.31 GPa 770 ksi ASTM Test
   1.93 GPa
@Temperature 120 °C
280 ksi
@Temperature 248 °F
ASTM Test
  2.40 GPa
@Temperature 65.0 °C
348 ksi
@Temperature 149 °F
ASTM Test
Izod Impact, Notched  0.590 J/cm
@Thickness 3.17 mm
1.11 ft-lb/in
@Thickness 0.125 in
ASTM Test
Izod Impact, Notched (ISO)  5.00 kJ/m² 2.38 ft-lb/in² ISO Test
Charpy Impact Unnotched  4.00 J/cm² 19.0 ft-lb/in² ISO 179
Charpy Impact, Notched  0.650 J/cm² 3.09 ft-lb/in² ISO 179
   0.550 J/cm²
@Temperature -30.0 °C
2.62 ft-lb/in²
@Temperature -22.0 °F
ISO 179
 
Electrical Properties Metric English Comments
Volume Resistivity  >= 1.00e+13 ohm-cm >= 1.00e+13 ohm-cm IEC 60093
Dielectric Constant    3.4
@Frequency 1.00e+6 Hz
3.4
@Frequency 1.00e+6 Hz
IEC 60250
  3.6
@Frequency 100 Hz
3.6
@Frequency 100 Hz
IEC 60250
  3.7
@Frequency 1.00e+6 Hz
3.7
@Frequency 1.00e+6 Hz
ASTM Data
  4.0
@Frequency 1e+9 Hz
4.0
@Frequency 1e+9 Hz
ASTM Data
Dielectric Strength  40.0 kV/mm 1020 kV/in IEC 60243-1
Dissipation Factor    0.010
@Frequency 100 Hz
0.010
@Frequency 100 Hz
IEC 60250
  0.010
@Frequency 1e+9 Hz
0.010
@Frequency 1e+9 Hz
ASTM Data
  0.010
@Frequency 1.00e+6 Hz
0.010
@Frequency 1.00e+6 Hz
ASTM Data
  0.020
@Frequency 1.00e+6 Hz
0.020
@Frequency 1.00e+6 Hz
IEC 60250
 
Thermal Properties Metric English Comments
CTE, linear  50.0 µm/m-°C
@Temperature -30.0 - 30.0 °C
27.8 µin/in-°F
@Temperature -22.0 - 86.0 °F
ASTM Test
CTE, linear, Parallel to Flow  39.0 µm/m-°C 21.7 µin/in-°F ISO 11359
CTE, linear, Transverse to Flow  78.0 µm/m-°C 43.3 µin/in-°F ISO 11359
Specific Heat Capacity  2.728 J/g-°C 0.6520 BTU/lb-°F Melt
Thermal Conductivity  0.230 W/m-K 1.60 BTU-in/hr-ft²-°F Melt
Melting Point  220 °C 428 °F 10 K/min
  220 °C 428 °F ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)  217 °C 423 °F ISO 75
Deflection Temperature at 1.8 MPa (264 psi)  195 °C 383 °F ISO 75
  200 °C 392 °F ASTM Test
Flammability, UL94    HB
@Thickness 0.750 mm
HB
@Thickness 0.0295 in
 
  HB
@Thickness 3.00 mm
HB
@Thickness 0.118 in
 
 
Processing Properties Metric English Comments
Melt Temperature  275 °C 527 °F Injection molding
Mold Temperature  95.0 °C 203 °F Injection molding
 
Descriptive Properties
Color Natural  
Commercial Status Active America  
Form Pellets  
Impact Modified No  
Primary Processing Technique Injection Molding  
Processing Injection Molding  
Special characteristic Heat stabilized or stable to heat  
UL.UL-C Yes
广泛用于制造机械、汽车、化学与电气装置的零件,如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外,还可用于制作医疗器械、体育用品、日用品等。
 
上海松翰塑化科技有限公司,供应原料,品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询:
联系人: 夏先生  
手  机:13501802636   
QQ    :205730283  
邮 箱 :205730283@qq.com 
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-26495.html

免责声明: 本文 PA6 8231G HS 14%玻璃、 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。