颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 1.70 % @Temperature 23.0 °C |
1.70 % @Temperature 73.4 °F |
50% RH; ISO 960 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | Eurotec | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Eurotec | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 | ||
| Tensile Modulus | 8.00 GPa | 1160 ksi | ISO 527 | ||
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A | ||
| 11.0 kJ/m² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | [10 K/min], ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 | ||
| Vicat Softening Point | 210 °C @Load 5.10 kg |
410 °F @Load 11.2 lb |
ISO 306 | ||
| Flammability, UL94 | V-1 @Thickness 0.750 mm |
V-1 @Thickness 0.0295 in |
|||
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||||
| Glow Wire Test | 800 °C @Thickness 2.00 mm |
1470 °F @Thickness 0.0787 in |
GWIT; IEC 60695 | ||
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI; IEC 60695 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 230 - 250 °C | 446 - 482 °F | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat | ||
| Mold Temperature | 40.0 - 90.0 °C | 104 - 194 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 | ||
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | |||
| De |
|||||
| Back Pressure | Low | ||||
| Injection Speed | Medium - Fast | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。