PA6 PF0057E 25%玻璃注射成型、_产品资讯

PA6 PF0057E 性状为半透明或不透明乳白色结晶形聚合物，具有可塑性。密度1．15g／cm3。熔点252℃。脆化温度-30℃。热分解温度大于350℃。连续耐热80-120℃,平衡吸水率2．5％。能耐酸、碱、大多数无机盐水溶液、卤代烷、烃类、酯类、酮类等腐蚀，但易溶于苯酚、甲酸等极性溶剂。具有优良的耐磨性、自润滑性，机械强度较高。但吸水性较大，因而尺寸稳定性较差。

颗粒：

、

物性表:

Physical Properties	Metric	English	Comments

Density	1.39 g/cc	0.0502 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm @Time 86400 sec	0.0010 - 0.0030 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.0090 - 0.013 cm/cm @Time 86400 sec	0.0090 - 0.013 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	145 MPa	21000 psi	ISO 527
Elongation at Break	3.0 %	3.0 %	ISO 527
Tensile Modulus	9.50 GPa	1380 ksi	1 mm/min; ISO 527
Flexural Strength	210 MPa	30500 psi	ISO 178
Flexural Modulus	8.00 GPa	1160 ksi	ISO 178
Izod Impact, Notched (ISO)	10.0 kJ/m²	4.76 ft-lb/in²	80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO)	54.0 kJ/m²	25.7 ft-lb/in²	80x10x4; ISO 180/1U

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	600 V	600 V	IEC 60112
Hot Wire Ignition, HWI	>= 120 sec @Thickness 0.800 mm	>= 120 sec @Thickness 0.0315 in	PLC 0
	>= 120 sec @Thickness 1.50 mm	>= 120 sec @Thickness 0.0591 in	PLC 0
	>= 120 sec @Thickness 1.60 mm	>= 120 sec @Thickness 0.0630 in	PLC 0
	>= 120 sec @Thickness 3.00 mm	>= 120 sec @Thickness 0.118 in	PLC 0
High Amp Arc Ignition, HAI	>= 120 arcs @Thickness 0.800 mm	>= 120 arcs @Thickness 0.0315 in	PLC 0
	>= 120 arcs @Thickness 1.50 mm	>= 120 arcs @Thickness 0.0591 in	PLC 0
	>= 120 arcs @Thickness 1.60 mm	>= 120 arcs @Thickness 0.0630 in	PLC 0
	>= 120 arcs @Thickness 3.00 mm	>= 120 arcs @Thickness 0.118 in	PLC 0

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.300 W/m-K	2.08 BTU-in/hr-ft²-°F	ISO 8302
Hot Ball Pressure Test	200 °C @Thickness 3.00 mm	392 °F @Thickness 0.118 in	IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi)	205 °C	401 °F	Flatw 80x10x4, sp=64 mm; ISO 75/Af
UL RTI, Electrical	140 °C @Thickness 0.800 mm	284 °F @Thickness 0.0315 in
	140 °C @Thickness 1.60 mm	284 °F @Thickness 0.0630 in
	140 °C @Thickness 1.60 mm	284 °F @Thickness 0.0630 in
	140 °C @Thickness 3.00 mm	284 °F @Thickness 0.118 in
UL RTI, Mechanical with Impact	105 °C @Thickness 0.800 mm	221 °F @Thickness 0.0315 in
	105 °C @Thickness 1.60 mm	221 °F @Thickness 0.0630 in
	105 °C @Thickness 1.60 mm	221 °F @Thickness 0.0630 in
	105 °C @Thickness 3.00 mm	221 °F @Thickness 0.118 in
UL RTI, Mechanical without Impact	140 °C @Thickness 0.800 mm	284 °F @Thickness 0.0315 in
	140 °C @Thickness 1.60 mm	284 °F @Thickness 0.0630 in
	140 °C @Thickness 1.60 mm	284 °F @Thickness 0.0630 in
	140 °C @Thickness 3.00 mm	284 °F @Thickness 0.118 in
Flammability, UL94	V-0 @Thickness 0.800 mm	V-0 @Thickness 0.0315 in	IEC 60695-11-10
	V-0 - 5VB @Thickness 1.60 mm	V-0 - 5VB @Thickness 0.0630 in	IEC 60695-11-10
	V-0 - 5VA @Thickness 1.60 mm	V-0 - 5VA @Thickness 0.0630 in	IEC 60695-11-10
	V-0 - 5VA @Thickness 3.00 mm	V-0 - 5VA @Thickness 0.118 in	IEC 60695-11-10
Glow Wire Test	775 °C @Thickness 0.800 mm	1430 °F @Thickness 0.0315 in	Glow-Wire Ignition; IEC 60695-2-13
	775 °C @Thickness 1.60 mm	1430 °F @Thickness 0.0630 in	Glow-Wire Ignition; IEC 60695-2-13
	775 °C @Thickness 1.60 mm	1430 °F @Thickness 0.0630 in	Glow-Wire Ignition; IEC 60695-2-13
	800 °C @Thickness 3.00 mm	1470 °F @Thickness 0.118 in	Glow-Wire Ignition; IEC 60695-2-13
	960 °C @Thickness 0.800 mm	1760 °F @Thickness 0.0315 in	Glow-Wire Flammability; IEC 60695-2-12
	960 °C @Thickness 1.60 mm	1760 °F @Thickness 0.0630 in	Glow-Wire Flammability; IEC 60695-2-12
	960 °C @Thickness 1.60 mm	1760 °F @Thickness 0.0630 in	Glow-Wire Flammability; IEC 60695-2-12
	960 °C @Thickness 3.00 mm	1760 °F @Thickness 0.118 in	Glow-Wire Flammability; IEC 60695-2-12

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	240 - 250 °C	464 - 482 °F	Zone 1
Middle Barrel Temperature	250 - 260 °C	482 - 500 °F	Zone 2
Front Barrel Temperature	250 - 270 °C	482 - 518 °F	Zone 3
Melt Temperature	250 - 270 °C	482 - 518 °F
Mold Temperature	50.0 - 90.0 °C	122 - 194 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	4.00 hour	4.00 hour
Moisture Content	0.20 %	0.20 %

Descriptive Properties
UL f1	f1

广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。

上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。

PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。

欢迎各位客户前来咨询：

联系人：夏先生

手机：13501802636

QQ ：205730283

邮箱：205730283@qq.com

PA6 PF0057E 25%玻璃 注射成型、

PA6 PF0057E 25%玻璃注射成型、