颗粒图：
、
、用途：
广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座。
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Moisture Absorption | 2.35 % @Temperature 23.0 °C |
2.35 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | 10 % @Temperature 23.0 °C |
10 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.015 cm/cm | 0.011 - 0.015 in/in | on Tensile Bar; E2P method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 121 | 121 | ISO 2039-2 |
| Hardness, H358/30 | 121 MPa | 17500 psi | ISO 2039-1 |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 15 % | 15 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 3.10 GPa | 450 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 100 MPa | 14500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.65 GPa | 384 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature -40.0 °C |
1.43 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A |
| 4.00 kJ/m² @Temperature -20.0 °C |
1.90 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A | |
| 4.00 kJ/m² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1A | |
| 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | >= 100 kJ/m² @Temperature 23.0 °C |
>= 47.6 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1U |
| >= 100 kJ/m² @Temperature -30.0 °C |
>= 47.6 ft-lb/in² @Temperature -22.0 °F |
80x10x4; ISO 180/1U | |
| Charpy Impact Unnotched | >= 27.0 J/cm² @Temperature 23.0 °C |
>= 128 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU |
| >= 27.0 J/cm² @Temperature -30.0 °C |
>= 128 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eU | |
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA |
| 0.300 J/cm² @Temperature -30.0 °C |
1.43 ft-lb/in² @Temperature -22.0 °F |
Edgew 80x10x4 sp=62; ISO 179/1eA | |
| Taber Abrasion, mg/1000 Cycles | 10 @Load 1.00 kg |
10 @Load 2.20 lb |
CS-17; E2P Method |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+16 ohm | >= 1.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 3.3 @Frequency 50.0 - 60.0 Hz |
3.3 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.20 mm |
406 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| Dissipation Factor | 0.0058 @Frequency 50.0 - 60.0 Hz |
0.0058 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.018 @Frequency 1.00e+6 Hz |
0.018 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| 600 V | 600 V | M; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ISO 8302 |
| Hot Ball Pressure Test | 123 - 127 °C | 253 - 261 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Vicat Softening Point | 215 °C | 419 °F | B/120; ISO 306 |
| 217 °C | 423 °F | B/50; ISO 306 | |
| UL RTI, Electrical | 65.0 °C | 149 °F | |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
||
| Oxygen Index | 24 % | 24 % | ISO 4589 |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 240 - 250 °C | 464 - 482 °F | |
| Zone 3 | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % | |