TPU CP80AS2 物性表：
个别产品成品图片
TPU CP80AS2 物性表：
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| 1.15 g/cc | 1.15 g/cc | PVC (80)/CP80AS2(20) | |
| 1.15 g/cc | 1.15 g/cc | PVC (70)/CP80AS2(30) | |
| 1.15 g/cc | 1.15 g/cc | PVC (50)/CP80AS2(50) | |
| Maximum Moisture Content | 0.020 | 0.020 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 62 | 62 | PVC (80)/CP80AS2(20) |
| 63 | 63 | PVC (70)/CP80AS2(30) | |
| 65 | 65 | PVC (50)/CP80AS2(50) | |
| 81 @Time 5.00 sec |
81 @Time 0.00139 hour |
ASTM D2240 | |
| Tensile Strength at Break | 15.9 MPa | 2310 psi | PVC (80)/CP80AS2(20) |
| 18.6 MPa | 2700 psi | PVC (70)/CP80AS2(30) | |
| 24.1 MPa | 3500 psi | PVC (50)/CP80AS2(50) | |
| Tensile Strength, Ultimate | 27.6 MPa | 4000 psi | ASTM D412 |
| Elongation at Break | 470 % | 470 % | Ultimate; ASTM D412 |
| 540 % | 540 % | PVC (80)/CP80AS2(20) | |
| 580 % | 580 % | PVC (70)/CP80AS2(30) | |
| 665 % | 665 % | PVC (50)/CP80AS2(50) | |
| 100% Modulus | 0.00390 GPa | 0.566 ksi | ASTM D412 |
| 300% Modulus | 0.00840 GPa | 1.22 ksi | ASTM D412 |
| Flexural Modulus | 0.00383 GPa | 0.555 ksi | PVC (80)/CP80AS2(20) |
| 0.00434 GPa | 0.630 ksi | PVC (70)/CP80AS2(30) | |
| 0.00579 GPa | 0.840 ksi | PVC (50)/CP80AS2(50) | |
| Tear Strength | 5.43 kN/m | 31.0 pli | Trouser, PVC (80)/CP80AS2(20) |
| 7.01 kN/m | 40.0 pli | Trouser, PVC (70)/CP80AS2(30) | |
| 11.7 kN/m | 67.0 pli | Trouser, PVC (50)/CP80AS2(50) | |
| 21.9 kN/m | 125 pli | Trouser; ASTM D470 | |
| Graves Tear Strength | 29.8 kN/m | 170 pli | PVC (80)/CP80AS2(20) |
| 33.3 kN/m | 190 pli | PVC (70)/CP80AS2(30) | |
| 47.3 kN/m | 270 pli | PVC (50)/CP80AS2(50) | |
| 63.1 kN/m | 360 pli | Die C; ASTM D624 | |
| Taber Abrasion, mg/1000 Cycles | 86 | 86 | PVC (50)/CP80AS2(50) |
| 128 | 128 | PVC (70)/CP80AS2(30) | |
| 146 | 146 | PVC (80)/CP80AS2(20) | |
| 14 @Load 1.00 kg |
14 @Load 2.20 lb |
H-18 wheel; ASTM D3389 | |
| Abrasion | 83 | 83 | [mm3], PVC (50)/CP80AS2(50) |
| 126 | 126 | [mm3], PVC (70)/CP80AS2(30) | |
| 148 | 148 | [mm3], PVC (80)/CP80AS2(20) | |
| Compression Set | 13 % | 13 % | PVC (80)/CP80AS2(20) |
| 16 % | 16 % | PVC (70)/CP80AS2(30) | |
| 19 % | 19 % | PVC (50)/CP80AS2(50) | |
| Tensile Set | 14 % | 14 % | PVC (50)/CP80AS2(50) |
| 16 % | 16 % | PVC (70)/CP80AS2(30) | |
| 19 % | 19 % | PVC (80)/CP80AS2(20) | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 140 °C | 284 °F | DSC |
| Glass Transition Temp, Tg | -30.0 °C | -22.0 °F | DSC |
| Processing Properties | Metric | English | Comments |
| Zone 1 | 170 °C | 338 °F | Extrusion |
| Zone 2 | 175 °C | 347 °F | Extrusion |
| Zone 3 | 180 °C | 356 °F | Extrusion |
| Zone 4 | 180 °C | 356 °F | Extrusion |
| Adapter Temperature | 180 °C | 356 °F | 5, Extrusion |
| Die Temperature | 180 °C | 356 °F | 6, Zone 1, Extrusion |
| 180 °C | 356 °F | Zone 2, Extrusion | |
| Drying Temperature | 150 °C | 302 °F | overnight |
| Dew Point | -40.0 °C | -40.0 °F |
|
应用介绍：
1．薄膜和片材（TPU具较好耐磨性、抗刺穿性、抗撕裂性、弹性、粘合性）（TPU薄膜应用在冬季服装、鞋类具有防寒、保暖、防水性能好等特性外还具有特别好的透气性）
2．管材（TPU具有高伸长率，良好耐水解和抗微生物性、耐油性、优异机械性能，如作消防水管内衬，输油管气动软管等）
3．鞋底，鞋邦等鞋材料（TPU具有突出耐磨性、抗刮性、耐刺穿性、抗纵向弯曲强度和低温冲击强度，其耐撕裂性和抗裂纹传播性是所有塑料中最好的。如作溜冰、滑雪靴、运动鞋、特种功能鞋等）
4．电线、电缆、光缆护套（TPU具良好耐磨性、耐环境、耐候性、耐腐蚀性、绝缘性、弹性和低温柔韧性等）
5．拉链片、高档塑料表带、表壳以及潜水表、礼品表等系列（TPU具有高弹、耐折、耐水性好手感舒适等）
6．机械制品和其它应用（如制造汽车部件、机械轴承、滚轮、输送带、橡塑筛网、工业胶管,垫圈,密封圈,游泳镜,冲浪板,表带,动物标牌,电器零部件,涂料,粘合剂,纤维等.)
上海松翰塑化科技有限公司供应产品，品质一流，TPV种类齐全。 公司理念你的要求就是我们的追求 。咨询人夏先生 电话：13751253137 QQ：205730283 我公司将给你最专业产品加工工艺指导及帮你解决加工工艺难题 欢迎你的咨询