颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Viscosity Measurement | 3.2 | 3.2 | Relative Viscosity; Sulfuric Acid |
| 82 | 82 | Relative Viscosity; Formic Acid | |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.540 J/cm | 1.01 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |
| Middle Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |
| Front Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Nozzle Temperature | 249 - 260 °C | 480 - 500 °F | |
| Melt Temperature | 249 - 260 °C | 480 - 500 °F | |
| Mold Temperature | 48.9 - 82.2 °C | 120 - 180 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | <= 0.080 % | <= 0.080 % | |
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。