颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ASTM D792 | ||
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0010 cm/cm | 0.00050 - 0.0010 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 155 MPa | 22500 psi | 5mm/min; ISO 527-2/1A | ||
| 203 MPa | 29500 psi | ASTM D638 | |||
| 87.6 MPa @Temperature 121 °C |
12700 psi @Temperature 250 °F |
ASTM D638 | |||
| 230.8 MPa @Temperature -40.0 °C |
33470 psi @Temperature -40.0 °F |
ASTM D638 | |||
| Elongation at Break | 1.78 % | 1.78 % | 5mm/min; ISO 527-2/1A | ||
| 2.6 % @Temperature 22.8 °C |
2.6 % @Temperature 73.0 °F |
ASTM D638 | |||
| 3.0 % @Temperature 121 °C |
3.0 % @Temperature 250 °F |
ASTM D638 | |||
| 3.1 % @Temperature -40.0 °C |
3.1 % @Temperature -40.0 °F |
ASTM D638 | |||
| Tensile Modulus | 9.51 GPa | 1380 ksi | 1mm/min; ISO 527-2/1A | ||
| 5.79 GPa @Temperature 121 °C |
840 ksi @Temperature 250 °F |
ASTM D638 | |||
| 9.65 GPa @Temperature -40.0 °C |
1400 ksi @Temperature -40.0 °F |
ASTM D638 | |||
| 10.3 GPa @Temperature 22.8 °C |
1500 ksi @Temperature 73.0 °F |
ASTM D638 | |||
| Flexural Strength | 290 MPa | 42100 psi | ASTM D790 | ||
| 130 MPa @Temperature 121 °C |
18800 psi @Temperature 250 °F |
ASTM D790 | |||
| 318.7 MPa @Temperature -40.0 °C |
46230 psi @Temperature -40.0 °F |
ASTM D790 | |||
| Flexural Modulus | 8.83 GPa | 1280 ksi | ISO 178 | ||
| 4.00 GPa @Temperature 121 °C |
580 ksi @Temperature 250 °F |
ASTM D790 | |||
| 9.03 GPa @Temperature 22.8 °C |
1310 ksi @Temperature 73.0 °F |
ASTM D790 | |||
| 9.79 GPa @Temperature -40.0 °C |
1420 ksi @Temperature -40.0 °F |
ASTM D790 | |||
| Izod Impact, Notched | 2.62 J/cm | 4.90 ft-lb/in | ASTM D256 | ||
| 2.35 J/cm @Temperature -40.0 °C |
4.40 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |||
| 3.84 J/cm @Temperature 121 °C |
7.20 ft-lb/in @Temperature 250 °F |
ASTM D256 | |||
| Charpy Impact, Notched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | ISO 75-1, -2 | ||
| 207 °C | 405 °F | ASTM D648 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| 80.0 - 100 °C | 176 - 212 °F | Cavity temperature | |||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Zone 1 | 260 - 270 °C | 500 - 518 °F | |||
| Zone 2 | 265 - 275 °C | 509 - 527 °F | |||
| Zone 3 | 270 - 280 °C | 518 - 536 °F | |||
| Zone 4 | 270 - 280 °C | 518 - 536 °F | |||
| Die Temperature | 270 - 280 °C | 518 - 536 °F | |||
| Melt Temperature | 270 - 280 °C | 518 - 536 °F | |||
| Mold Temperature | 85.0 - 95.0 °C | 185 - 203 °F | |||
| Drying Temperature | 70.0 - 80.0 °C | 158 - 176 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | 0.18 % | 0.18 % | Necessary low maximum residual | ||
| Dew Point | <= -30.0 °C | <= -22.0 °F | Pre-drying | ||
| De |
|||||
| Injection molding | Yes | ||||
| Longer pre-drying times/storage | Material can be over dried and may discolor. | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。