| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 101 MPa | 14600 psi | ASTM D638 |
| Flexural Strength | 155 MPa | 22500 psi | ASTM D790 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm @Thickness 3.20 mm |
1.50 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Charpy Impact Unnotched | 4.80 J/cm² | 22.8 ft-lb/in² | ISO179 |
| Charpy Impact, Notched | 0.950 J/cm² | 4.52 ft-lb/in² | ISO179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
ASTM D150 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm |
635 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Dissipation Factor | 0.029 @Frequency 1e+6 Hz |
0.029 @Frequency 1e+6 Hz |
ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 168 °C | 334 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
|
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 210 - 220 °C | 410 - 428 °F | |
| Middle Barrel Temperature | 235 - 245 °C | 455 - 473 °F | |
| Front Barrel Temperature | 245 - 255 °C | 473 - 491 °F | |
| Nozzle Temperature | 240 - 245 °C | 464 - 473 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 130 °C | 266 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。