| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.52 g/cc @Temperature 23.0 °C |
1.52 g/cc @Temperature 73.4 °F |
ASTM D792 | ||
| Water Absorption | 0.60 % @Temperature 23.0 °C, Time 86400 sec |
0.60 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 | ||
| Linear Mold Shrinkage | 0.0040 - 0.0090 cm/cm @Temperature 23.0 °C |
0.0040 - 0.0090 in/in @Temperature 73.4 °F |
ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 120 | 120 | ASTM D785 | ||
| Tensile Strength at Break | 145 MPa | 21000 psi | 10mm/min; ASTM D638 | ||
| Elongation at Break | 2.1 % | 2.1 % | 10mm/min; ASTM D638 | ||
| Flexural Strength | 210 MPa | 30500 psi | 2mm/min; ASTM D790 | ||
| Flexural Modulus | 8.50 GPa | 1230 ksi | 2mm/min; ASTM D790 | ||
| Izod Impact, Notched | 1.15 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
2.15 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C @Thickness 6.40 mm |
428 °F @Thickness 0.252 in |
ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C @Thickness 6.40 mm |
419 °F @Thickness 0.252 in |
ASTM D648 | ||
| Flammability, UL94 | V-0 @Thickness 0.900 mm |
V-0 @Thickness 0.0354 in |
|||
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 300 °C | <= 572 °F | |||
| Rear Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Start Point: 235°C | ||
| Middle Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Start Point: 255°C | ||
| Front Barrel Temperature | 255 - 275 °C | 491 - 527 °F | Start Point: 265°C | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Start Point: 265°C | ||
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | Start Point: 50°C | ||
| Drying Temperature | 90.0 - 110 °C @Time 14400 - 21600 sec |
194 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry | ||
| De |
|||||
| Glass Fiber Content (%) | 30 | ||||
| Injection Speed | Moderate to High |
||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。