颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 2.56 g/cc | 0.0925 lb/in³ | |||
| Linear Mold Shrinkage, Flow | 0.00350 - 0.00550 cm/cm | 0.00350 - 0.00550 in/in | |||
| Linear Mold Shrinkage, Transverse | 0.00400 - 0.00600 cm/cm | 0.00400 - 0.00600 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 80.0 MPa | 11600 psi | |||
| Elongation at Break | 1.50 % | 1.50 % | |||
| Tensile Modulus | 11.4 GPa | 1650 ksi | |||
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | |||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | |||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 1.70 W/m-K | 11.8 BTU-in/hr-ft²-°F | Longitudinal | ||
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | |||
| Vicat Softening Point | 195 °C @Load 5.00 kg |
383 °F @Load 11.0 lb |
|||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 290 °C | 482 - 554 °F | |||
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |||
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
|||
| De |
|||||
| ISO Shrinkage - Pressure | 60 MPa | ||||
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。