颗粒图：
、
、用途：
广泛应用于机械、仪器仪表、汽车部件、电子电气、铁路、家电、通讯、纺机、体育休闲用品、油管、油箱及一些精密工程制品。
电子电器：连接器、卷线轴、计时器、护盖断路器、开关壳座。
汽车： 散热风扇、门把、油箱盖、进气隔栅、水箱护盖、灯座。
工业零件：椅座、自行车输框、溜冰鞋底座、纺织梭、踏板、滑输。
上海松翰塑化科技有限公司，供应原料，品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询：
联系人： 夏先生
手 机：13501802636
QQ ：205730283
邮 箱 ：205730283@qq.com
物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Water Absorption | 1.4 % | 1.4 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.016 cm/cm @Thickness 3.20 mm |
0.012 - 0.016 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 114 | 114 | ASTM D785 |
| Tensile Strength, Yield | 66.7 MPa @Thickness 3.20 mm |
9670 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 80 % @Thickness 3.20 mm |
80 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 83.4 MPa @Thickness 3.20 mm |
12100 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 2.16 GPa @Thickness 3.20 mm |
313 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 1.67 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
3.12 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.8 @Frequency 1.00e+6 Hz |
2.8 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 19.0 kV/mm @Thickness 1.00 mm |
483 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Arc Resistance | 195 sec | 195 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C @Thickness 6.40 mm |
302 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C @Thickness 6.40 mm |
122 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 230 - 260 °C | 446 - 500 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 270 °C | 464 - 518 °F | Injection Molding |
| Front Barrel Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Nozzle Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | Injection Molding |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |