颗粒：
、
、物性表:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Water Absorption | 0.50 % @Temperature 23.0 °C, Time 86400 sec |
0.50 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 41.7 MPa @Thickness 3.20 mm |
6040 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 330 % @Thickness 3.20 mm |
330 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 20.1 MPa @Thickness 6.40 mm |
2920 psi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 0.481 GPa @Thickness 6.40 mm |
69.7 ksi @Thickness 0.252 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 1.37 J/cm @Thickness 6.40 mm, Temperature -40.0 °C |
2.57 ft-lb/in @Thickness 0.252 in, Temperature -40.0 °F |
ASTM D256 |
| NB @Thickness 6.40 mm, Temperature 23.0 °C |
NB @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 235 - 250 °C | 455 - 482 °F | Injection Molding |
| Middle Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | Injection Molding |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Melt Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。