pa46 TQ261F2_产品资讯_塑胶原料之家

物理性能测试标准数据单位
比重ISO 11831.22g/cm³
吸水率
(23°C,50RH,2.00mm)ISO 623.10%

机械性能测试标准数据(常态)单位
拉伸强度
23°CISO 527-2115Mpa
断裂伸长率
23°CISO 527-24.00%
拉伸模量
23°CISO 527-24500Mpa
简支梁缺口冲击强度
23°CISO 179/1eA8.00kJ/m²

热性能测试标准数据单位
热变形温度
1.80MPa 未退火ISO 75-2/Af270°C
维卡软化温度
熔融温度ISO 11357-3295°C

注塑成型条件建议值单位
干燥温度80°C
干燥时间4-8Hr
注塑温度
螺筒后部温度280-320°C
螺筒中部温度300-320°C
螺筒前部温度300-320°C
模头温度300-320°C
模具温度80-120°C

Physical Properties	Metric	English	Comments
物性表：
Density	1.35 g/cc	0.0488 lb/in³	dry; ISO 1183
Moisture Absorption	2.25 %	2.25 %	Sim. To ISO 62
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	Sim. To ISO 294-4
Linear Mold Shrinkage, Transverse	0.0060 cm/cm	0.0060 in/in	Sim. To ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	160 MPa	23200 psi	cond; ISO 527-1/-2
	240 MPa	34800 psi	dry; ISO 527-1/-2
	90.0 MPa @Temperature 200 °C	13100 psi @Temperature 392 °F	ISO 527-1/-2
	100 MPa @Temperature 180 °C	14500 psi @Temperature 356 °F	ISO 527-1/-2
	110 MPa @Temperature 160 °C	16000 psi @Temperature 320 °F	ISO 527-1/-2
	130 MPa @Temperature 120 °C	18900 psi @Temperature 248 °F	ISO 527-1/-2
Elongation at Break	1.6 %	1.6 %	dry; ISO 527-1/-2
	3.5 %	3.5 %	cond; ISO 527-1/-2
	3.1 % @Temperature 120 °C	3.1 % @Temperature 248 °F	ISO 527-1/-2
	3.1 % @Temperature 160 °C	3.1 % @Temperature 320 °F	ISO 527-1/-2
	3.1 % @Temperature 180 °C	3.1 % @Temperature 356 °F	ISO 527-1/-2
	3.1 % @Temperature 200 °C	3.1 % @Temperature 392 °F	ISO 527-1/-2
Tensile Modulus	14.5 GPa	2100 ksi	cond; ISO 527-1/-2
	24.0 GPa	3480 ksi	dry; ISO 527-1/-2
	10.0 GPa @Temperature 200 °C	1450 ksi @Temperature 392 °F	ISO 527-1/-2
	10.5 GPa @Temperature 180 °C	1520 ksi @Temperature 356 °F	ISO 527-1/-2
	11.0 GPa @Temperature 160 °C	1600 ksi @Temperature 320 °F	ISO 527-1/-2
	12.5 GPa @Temperature 120 °C	1810 ksi @Temperature 248 °F	ISO 527-1/-2
Fatigue Strength	57.0 MPa @# of Cycles 1.00e+7 , Temperature 140 °C	8270 psi @# of Cycles 1.00e+7 , Temperature 284 °F	R = 0.1, 8 Hz, dry
	66.0 MPa @# of Cycles 1.00e+6 , Temperature 140 °C	9570 psi @# of Cycles 1.00e+6 , Temperature 284 °F	R = 0.1, 8 Hz, dry
	76.0 MPa @# of Cycles 100000 , Temperature 140 °C	11000 psi @# of Cycles 100000 , Temperature 284 °F	R = 0.1, 8 Hz, dry
	87.0 MPa @# of Cycles 10000 , Temperature 140 °C	12600 psi @# of Cycles 10000 , Temperature 284 °F	R = 0.1, 8 Hz, dry
	100 MPa @# of Cycles 1000 , Temperature 140 °C	14500 psi @# of Cycles 1000 , Temperature 284 °F	R = 0.1, 8 Hz, dry
Charpy Impact Unnotched	5.00 J/cm² @Temperature 23.0 °C	23.8 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eU
	5.00 J/cm² @Temperature -30.0 °C	23.8 ft-lb/in² @Temperature -22.0 °F	dry; ISO 179/1eU
	5.50 J/cm² @Temperature -30.0 °C	26.2 ft-lb/in² @Temperature -22.0 °F	cond; ISO 179/1eU
	8.00 J/cm² @Temperature 23.0 °C	38.1 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eU
Charpy Impact, Notched	0.600 J/cm² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	cond; ISO 179/1eA
	0.600 J/cm² @Temperature 23.0 °C	2.86 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eA
	0.600 J/cm² @Temperature -30.0 °C	2.86 ft-lb/in² @Temperature -22.0 °F	dry; ISO 179/1eA
	1.30 J/cm² @Temperature 23.0 °C	6.19 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	25.0 µm/m-°C	13.9 µin/in-°F	dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow	35.0 µm/m-°C	19.4 µin/in-°F	dry; ISO 11359-1/-2
Melting Point	295 °C	563 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	290 °C	554 °F	dry; ISO 75-1/-2