| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in³ | dry; ISO 1183 |
| Moisture Absorption | 1.25 % | 1.25 % | Sim. To ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | Sim. To ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | Sim. To ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | cond; ISO 527-1/-2 |
| 195 MPa | 28300 psi | dry; ISO 527-1/-2 | |
| 90.0 MPa @Temperature 160 °C |
13100 psi @Temperature 320 °F |
ISO 527-1/-2 | |
| 110 MPa @Temperature 120 °C |
16000 psi @Temperature 248 °F |
ISO 527-1/-2 | |
| Elongation at Break | 2.0 % | 2.0 % | dry; ISO 527-1/-2 |
| 2.6 % | 2.6 % | cond; ISO 527-1/-2 | |
| 3.0 % @Temperature 120 °C |
3.0 % @Temperature 248 °F |
ISO 527-1/-2 | |
| 3.0 % @Temperature 160 °C |
3.0 % @Temperature 320 °F |
ISO 527-1/-2 | |
| Tensile Modulus | 12.0 GPa | 1740 ksi | cond; ISO 527-1/-2 |
| 15.0 GPa | 2180 ksi | dry; ISO 527-1/-2 | |
| 6.50 GPa @Temperature 160 °C |
943 ksi @Temperature 320 °F |
ISO 527-1/-2 | |
| 9.50 GPa @Temperature 120 °C |
1380 ksi @Temperature 248 °F |
ISO 527-1/-2 | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | cond; ISO 178 |
| 13.0 GPa | 1890 ksi | dry; ISO 178 | |
| 5.50 GPa @Temperature 160 °C |
798 ksi @Temperature 320 °F |
ISO 178 | |
| 8.50 GPa @Temperature 120 °C |
1230 ksi @Temperature 248 °F |
ISO 178 | |
| Izod Impact Resistance | 1.20 J/cm² @Temperature -40.0 °C |
5.71 ft-lb/in² @Temperature -40.0 °F |
cond; ISO 180/1A |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 180/1A | |
| 1.20 J/cm² @Temperature -40.0 °C |
5.71 ft-lb/in² @Temperature -40.0 °F |
dry; ISO 180/1A | |
| 1.30 J/cm² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 180/1A | |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
dry; ISO 179/1eA |
| 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
dry; ISO 179/1eA | |
| 1.10 J/cm² @Temperature -30.0 °C |
5.23 ft-lb/in² @Temperature -22.0 °F |
cond; ISO 179/1eA | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
cond; ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | cond; IEC 60093 |
| >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | dry; IEC 60093 | |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | cond; IEC 60243-1 |
| 30.0 kV/mm | 762 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 350 V | 350 V | dry; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | dry; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | dry; ISO 11359-1/-2 |
| Melting Point | 295 °C | 563 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 163 °C | 325 °F | 5000 hours Thermal Index; IEC 60216/ISO 527-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 290 °C | 554 °F | dry; ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
dry; IEC 60695-11-10 |
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
dry; IEC 60695-11-10 |
|
广泛用于制造机械、汽车、化学与电气装置的零件，如齿轮、滚子、滑轮、辊轴、泵体中叶轮、风扇叶片、高压密封围、阀座、垫片、衬套、各种把手、支撑架、电线包层等。亦可制成薄膜用作包装材料。此外，还可用于制作医疗器械、体育用品、日用品等。