PTS 15GFR-BK PBT- 阻燃 15%玻璃、

PTS 15GFR-BK在相对湿度较高、十分潮湿的情况下,PTS 15GFR-BK 由于潮湿易引起塑性降低,电器节点处容易引起腐蚀,常可使用改性PBT。在80℃、90%相对湿度下,PBT仍能正常使用,并且效果很好。
PTS 15GFR-BK 与增强PA、PC、POM在汽车制造业中的竞争十分激烈,PA易吸水,PC的耐热性耐药性不及PBT;在汽车用途接管方面,由于PBT的抗吸水性优于PA,将会逐渐取代PA。
颗粒图:3cb92a240a17ac78-f9799ed1752670e2-b7b9ebca3e74f0a441b826101e142cc7 、
 
物性表:
 
Physical Properties Metric English Comments
Specific Gravity  1.30 g/cc 1.30 g/cc  
Water Absorption  0.080 %
@Time 86400 sec
0.080 %
@Time 24.0 hour
 
Viscosity  200 cP
@Shear Rate 1000 1/s
200 cP
@Shear Rate 1000 1/s
CR Viscosity at 6 Min; Capillary Rheometer
Linear Mold Shrinkage, Flow  0.010 cm/cm 0.010 in/in 410°C nozzle, 220°C mold
Linear Mold Shrinkage, Transverse  0.013 cm/cm 0.013 in/in 410°C nozzle, 220°C mold
Crystallinity  40 % 40 % DSC
 
Mechanical Properties Metric English Comments
Hardness, Rockwell M  103 103 ASTM D785
Hardness, Shore D  86 86  
Tensile Strength, Yield   25.0 MPa
@Temperature 250 °C
3630 psi
@Temperature 482 °F
ASTM D638
  35.0 MPa
@Temperature 200 °C
5080 psi
@Temperature 392 °F
ASTM D638
  55.0 MPa
@Temperature 150 °C
7980 psi
@Temperature 302 °F
ASTM D638
  75.0 MPa
@Temperature 100 °C
10900 psi
@Temperature 212 °F
ASTM D638
  100 - 110 MPa
@Temperature 23.0 °C
14500 - 16000 psi
@Temperature 73.4 °F
ASTM D638
  140 MPa
@Temperature -10.0 °C
20300 psi
@Temperature 14.0 °F
ASTM D638
  160 MPa
@Temperature -50.0 °C
23200 psi
@Temperature -58.0 °F
ASTM D638
Elongation at Break  10 - 15 % 10 - 15 % ASTM D638
Tensile Modulus  4.20 GPa 609 ksi ASTM D638
Flexural Strength  185 - 190 MPa 26800 - 27600 psi ASTM D790
Flexural Modulus  4.10 GPa 595 ksi ASTM D790
Izod Impact, Notched  0.550 - 0.600 J/cm 1.03 - 1.12 ft-lb/in ASTM D256
Izod Impact, Unnotched  NB NB ASTM D256
 
Electrical Properties Metric English Comments
Volume Resistivity  1.00e+16 ohm-cm 1.00e+16 ohm-cm ASTM D257
Surface Resistivity per Square  1.00e+16 ohm 1.00e+16 ohm ASTM D257
Dielectric Strength  16.0 kV/mm
@Thickness 3.20 mm
406 kV/in
@Thickness 0.126 in
ASTM D149
Arc Resistance  175 sec 175 sec at 500 Volts; ASTM D495
Comparative Tracking Index  145 V 145 V per 50 drops; ASTM D3638
 
Thermal Properties Metric English Comments
Melting Point  370 - 372 °C 698 - 702 °F DSC
Deflection Temperature at 1.8 MPa (264 psi)  167 °C 333 °F  
Glass Transition Temp, Tg  152 - 154 °C 306 - 309 °F DSC/onset
Flammability, UL94  V-0
@Thickness 0.800 mm
V-0
@Thickness 0.0315 in
 
 
Processing Properties Metric English Comments
Processing Temperature  385 - 410 °C 725 - 770 °F  
Nozzle Temperature  410 °C 770 °F  
Mold Temperature  200 - 220 °C 392 - 428 °F  
Drying Temperature  150 °C 302 °F  
Dry Time  4 - 6 hour 4 - 6 hour  
 
Descriptive Properties
Hopper/ Throat Temperature 60-80°C
 
上海松翰塑化科技有限公司,供应原料,品质真实,物实价廉。
PA6T,46,9T、PC、PC/ABS、PBT、ABS、PPA、PPS、POM、PMMA、TPE、PPO、LCP液晶聚合物。
欢迎各位客户前来咨询:
联系人: 夏先生  
手  机:13501802636   
QQ    :205730283  
邮 箱 :205730283@qq.com 
 

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/news/

本文链接: http://www.su-jiao.com/news/show-27613.html

免责声明: 本文 PTS 15GFR-BK PBT- 阻燃 15%玻璃、 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家